Recently, titanium dioxide (TiO₂) nanomaterials have gained increased attention because of their cost-effective, safe, stable, non-toxic, non-carcinogenic, photocatalytic, bactericidal, biomedical, industrial and waste-water treatment applications. The aim of the present work is the synthesis of electrospun TiO₂ nanofibers (NFs) in the presence of different amounts of air–argon mixtures using sol-gel and electrospinning approaches. The physicochemical properties of the synthesized NFs were examined by scanning and transmission electron microscopies (SEM and TEM) coupled with energy-dispersive X-ray spectroscopy (EDX), ultraviolet-visible spectroscopy and thermogravimetric analyzer (TGA). The antibacterial and antibiofilm activity of synthesized NFs against Gram-negative Pseudomonas aeruginosa and Gram-positive methicillin-resistant Staphylococcusaureus (MRSA) was investigated by determining their minimum bacteriostatic and bactericidal values. The topological and morphological alteration caused by TiO₂ NFs in bacterial cells was further analyzed by SEM. TiO₂ NFs that were calcined in a 25% air-75% argon mixture showed maximum antibacterial and antibiofilm activities. The minimum inhibitory concentration (MIC)/minimum bactericidal concentration (MBC) value of TiO₂ NFs against P. aeruginosa was 3 and 6 mg/mL and that for MRSA was 6 and 12 mg/mL, respectively. The MIC/MBC and SEM results show that TiO₂ NFs were more active against Gram-negative P. aeruginosa cells than Gram-positive S. aureus. The inhibition of biofilm formation by TiO₂ NFs was investigated quantitatively by tissue culture plate method using crystal violet assay and it was found that TiO₂ NFs inhibited biofilm formation by MRSA and P. aeruginosa in a dose-dependent manner. TiO₂ NFs calcined in a 25% air-75% argon mixture exhibited maximum biofilm formation inhibition of 75.2% for MRSA and 72.3% for P. aeruginosa at 2 mg/mL, respectively. The antibacterial and antibiofilm results suggest that TiO₂ NFs can be used to coat various inanimate objects, in food packaging and in waste-water treatment and purification to prevent bacterial growth and biofilm formation.

TiO2 nanofibers were prepared within polyvinylpyrrolidone (PVP) polymer using a combination of sol–gel and electrospinning techniques. Based on a Taguchi design of experiment (DoE) method, the effects of sol–gel and electrospinning on the TiO2/PVP nanofibers’ diameter, including titanium isopropoxide (TiP) concentration, flow rate, needle tip-to-collector distance, and applied voltage were evaluated. The analysis of DoE experiments for nanofiber diameters demonstrated that TiP concentration was the most significant factor. An optimum combination to obtain smallest diameters was also determined with a minimum variation for electrospun TiO2/PVP nanofibers. The optimum combination was determined to be a 60% TiP concentration, at a flow rate of 1ml/h, with the needle tip-to-collector distance at 11cm (position a), and the applied voltage of 18kV. This combination was further validated by conducting a confirmation experiment that used two different needles to study the effect of needle size. The average nanofiber diameter was approximately the same for both needle sizes in good accordance with the optimum condition estimated by the Taguchi DoE method