In this paper, the welding thermal cycle process of deep-sea pipeline steel was investigated by welding thermal simulation. The microstructure evolution, crystallology and second-phase precipitation behavior of the soft zone of the heat-affected zone (HAZ) were characterized and analyzed by combining scanning electron microscopy, electron back-scattered diffraction, transmission electron microscopy and hardness testing. The results show that HAZ softening appeared in the fine-grained zone with a peak temperature of 900–1000 °C for deep-sea pipeline steel, the base metal microstructure of which was the polygonal ferrite and acicular ferrite. Using V microalloying and low welding heat input could effectively decrease the softening of the HAZ fine-grained region, which was achieved by reducing the effective grain size, increasing the proportion of the dislocation substructures, and precipitating the nanoscale second-phase particles.

With the rapid development of hydrogen pipelines, their safety issues have become increasingly prominent. In order to evaluate the properties of pipeline materials under a high-pressure hydrogen environment, this study investigates the hydrogen embrittlement sensitivity of X70 welded pipe in a 10 MPa high-pressure hydrogen environment, using slow strain rate testing (SSRT) and low-cycle fatigue (LCF) analysis. The microstructure, slow tensile and fatigue fracture morphology of base metal (BM) and weld metal (WM) were characterized and analyzed by means of ultra-depth microscope, scanning electron microscope (SEM), electron backscattering diffraction (EBSD), and transmission electron microscope (TEM). Results indicate that while the high-pressure hydrogen environment has minimal impact on ultimate tensile strength (UTS) for both BM and WM, it significantly decreases reduction of area (RA) and elongation (EL), with RA reduction in WM exceeding that in BM. Under the nitrogen environment, the slow tensile fracture of X70 pipeline steel BM and WM is a typical ductile fracture, while under the high-pressure hydrogen environment, the unevenness of the slow tensile fracture increased, and a large number of microcracks appeared on the fracture surface and edges, with the fracture mode changing to ductile fracture + quasi-cleavage fracture. In addition, the high-pressure hydrogen environment reduces the fatigue life of the BM and WM of X70 pipeline steel, and the fatigue life of the WM decreases more than that of the BM as well. Compared to the nitrogen environment, the fatigue fracture specimens of BM and WM in the hydrogen environment showed quasi-cleavage fracture patterns, and the fracture area in the instantaneous fracture zone (IFZ) was significantly reduced. Compared with the BM of X70 pipeline steel, although the effective grain size of the WM is smaller, WM’s microstructure, with larger Martensite/austenite (M/A) constituents and MnS and Al-rich oxides, contributes to a heightened embrittlement sensitivity. In contrast, the second-phase precipitation of nanosized Nb, V, and Ti composite carbon-nitride in the BM acts as an effective irreversible hydrogen trap, which can significantly reduce the hydrogen embrittlement sensitivity.

In this paper, a series of low-temperature CVN (Charpy V-notch impact test) and DWTT (drop-weight tear test) experiments were carried out to deal with the intensifying contradiction of strength and toughness of ultra-high-strength pipeline steel. The fracture behavior and toughening mechanisms of ultra-high-strength pipeline steel were investigated using scanning electron microscopy, transmission electron microscopy and backscattered electron diffraction systems. The results show that DWTT fractures in ultra-high-strength pipeline steel had a variety of unconventional morphological features compared to CVN fractures, including ridge protrusion in ductile fracture conditions and a large-size fracture platform in brittle fracture conditions. Therefore, DWTT fractures contained more information about the material fracturing process, and could better reflect the actual process of material fracturing. In ultra-high-strength pipeline steel, fine-grained granular bainite caused cracks to undergo large deflections or frequent small transitions, which consumed additional energy and improved toughness. In contrast, large-sized granular bainite, which consisted of low-angle grain boundaries, did not effectively prevent crack propagation when it encountered cracks, which was not conducive to improved toughness. Moreover, the M/A constituents in large-sized granular bainite aggregated, cracked, or fell off, which could easily lead to the formation of microcracks and was also detrimental to toughening.

In this paper, the influence of Cr element on the mechanical properties of welded joints of gas-shielded solid wire used in oil and gas long-distance pipelines was studied by means of tensile test, impact test, and hardness test, and the microstructure and crack propagation path of weld were characterized by means of an optical microscope, scanning electron microscope, and electron backscattering diffraction. The results show that with the addition of Cr, the strength and toughness of the weld are significantly improved, in which the tensile strength is increased from 607 MPa to 656 MPa, and the impact toughness is increased from 126.37 J to 223.79 J. The proportion of the ferrite side plate in the weld structure is reduced by about 20%, and the effective grain size of acicular ferrite is reduced by about 15%. The reason is that the addition of the Cr element improves the hardenability of the weld structure, inhibits the formation of the ferrite side plate, and promotes the effective refinement of acicular ferrite, which increases the proportion of high-angle grain boundaries in the weld, effectively hindering the crack propagation, improves the crack propagation work, and thus improves the strength and toughness of the weld.

The existing studies mainly focus on the coarse-grained heat-affected zone and the inter-critically reheated coarse-grained heat-affected zone, while the studies on other sub-zones are relatively low. Meanwhile, the studies on the Cr element in steel mainly focus on the influence of the Cr element on strength and hardness; however, its mechanism is not very clear. Therefore, three kinds of X80 experimental steels with different Cr contents (0 wt.%, 0.13 wt.%, and 0.40 wt.%) were designed in this paper. The thermal simulation experiments on the supercritically coarse-grained heat-affected zone (SCCGHAZ) were carried out using a Gleeble-3500 thermal simulator. The effects of Cr on the microstructure and toughness of SCCGHAZ were systematically investigated through Charpy impact tests and microstructural characterization techniques. The results indicate that the microstructures of the three Cr-containing X80 experimental steels in SCCGHAZ are predominantly composed of fine granular bainite. However, impact tests at −10 °C show that the SCCGHAZs of 0 wt.% and 0.13 wt.% Cr steel exhibit higher impact energy, while that of the 0.40 wt.% Cr steel demonstrates significantly reduced energy impact (<100 J). Microstructural characterization reveals that the impact toughness of the SCCGHAZ in X80 steel is correlated with microstructural features, including effective grain size, grain boundary angles, and the volume fraction and shape of martensite–austenite (M-A) constituents. Among these factors, the volume fraction of M-A constituents substantially influences toughness. It was found that island-shaped M-A constituents inhibit crack propagation, whereas blocky M-A constituents impair toughness.