In this paper, the influence of Cr element on the mechanical properties of welded joints of gas-shielded solid wire used in oil and gas long-distance pipelines was studied by means of tensile test, impact test, and hardness test, and the microstructure and crack propagation path of weld were characterized by means of an optical microscope, scanning electron microscope, and electron backscattering diffraction. The results show that with the addition of Cr, the strength and toughness of the weld are significantly improved, in which the tensile strength is increased from 607 MPa to 656 MPa, and the impact toughness is increased from 126.37 J to 223.79 J. The proportion of the ferrite side plate in the weld structure is reduced by about 20%, and the effective grain size of acicular ferrite is reduced by about 15%. The reason is that the addition of the Cr element improves the hardenability of the weld structure, inhibits the formation of the ferrite side plate, and promotes the effective refinement of acicular ferrite, which increases the proportion of high-angle grain boundaries in the weld, effectively hindering the crack propagation, improves the crack propagation work, and thus improves the strength and toughness of the weld.

This study systematically investigates the influence mechanism of the element Cr on the mechanical properties of the heat-affected zone in pipeline steels for supercritical CO₂ transportation. Microstructural evolution in the heat affected-zone was characterized through thermal simulation tests, Charpy impact testing (−10 °C), and microhardness measurements, complemented by multiscale microscopic analyses (optical microscopy, scanning electron microscopy, electron backscatter diffraction, and transmission electron microscopy). The results demonstrate that Cr addition enhances the base metal’s resistance to supercritical CO₂ corrosion but reduces its low-temperature impact toughness from 277 J to 235 J at −10 °C. Notably, the intercritical heat-affected zone exhibits severe embrittlement, with impact energy plummeting from 235 J (base metal) to 77 J. Microstructural analysis reveals that Cr interacts with carbon to form stable carbonitride particles, which reduce the free carbon concentration and diffusion coefficient in austenite, thereby inducing heterogeneous austenitization. Undissolved carbonitrides pin grain boundaries, creating carbon concentration gradients. During rapid cooling, these localized carbon-enriched microregions preferentially transform into core–shell-structured M-A constituent, characterized by a micro-twin containing retained austenite core encapsulated by high hardness lath martensite. The synergistic interaction between micro-twins and interfacial thermal mismatch stress induces localized stress concentration, triggering microcrack nucleation and subsequent toughness degradation.