Titanium alloy Ti6Al4V has been widely applied to medical, automotive, and aerospace industries due to its excellent properties such as high strength and excellent corrosion resistance. On the other hand, additive manufacturing (AM) technology can give the freedom of design of the products. In order to spread the AMed products, the joining of AMed and wrought products are required, and it is important to understand the joint characteristics. In this study, butt welding of Ti6Al4V plate was conducted by fiber laser in argon shielding, and the joint characteristics of laser weld wrought/wrought, AMed/AMed, and AMed/wrought Ti6Al4V plates were experimentally investigated. The AMed plate has higher tensile strength than wrought plate but the elongation of AMed plate is smaller, since AMed plate has α’ martensite due to rapid cooling during laser irradiation in AM process. Then, the laser weld joint of AMed/AMed plates has higher tensile strength, but smaller elongation than that of wrought/wrought plates. The weld joint of AMed/wrought plates shows good welding state, since small heat input leads to formation of small weld bead with higher hardness between wrought and AMed plates.

In recent years, CVD diamond-coated tungsten carbide (WC-Co) tools have been widely utilized due to their benefits in the machining of non-ferrous alloys and polymer composite materials, especially carbon-fiber-reinforced plastics (CFRPs). The reconditioning of such coated tools is economically attractive due to their high cost and short tool life. The decoating of the remaining diamond film from the used tools and the subsequent surface preparation by wet chemical pretreatment are essential steps for new CVD diamond film formation. Previously, it was shown that reactive ion beam etching (RIBE) could effectively remove CVD diamond films. However, some degree of WC-Co tool substrate damage is expected due to the high ion energy in RIBE and the chemical activity in wet etching. This study addresses the effects of RIBE decoating and surface pretreatment steps on WC-Co tools with a complex shape in terms of the ion-induced surface damage, geometry alteration, and adhesion of a subsequently re-applied CVD diamond film. Moreover, the cutting performance of the tools subjected to the RIBE decoating and repeated film deposition was studied via CFRP cutting tests. It has been shown that the RIBE decoated and recoated tools had a high level of cutting performance comparable to the new tools.

Laser micro-grooving has excellent potential to improve the surface properties of metals. In this study, high-speed micro-grooving of the surfaces of mild steel SS400 and aluminum alloy A1050 was investigated using a single-mode continuous-wave fiber laser with an average power of 200 W. Experiments were conducted at laser beam scanning speeds of 1 to 6 m/s. The incident angle of the laser beam in the plane perpendicular to the scanning axis was varied from 0 to 60°. A relatively deep groove (approximately 30 µm in depth) and a high upheaval (10 µm in height) were formed along the scanning line at an incident angle of 45° on the SS400, whereas only shallow grooves were formed on A1050. The micro-groove formation mechanism was discussed on the basis of high-speed camera observation, groove shapes, and the thermophysical properties of the metal. Asymmetric molten metal flow and solidification around the keyhole are thought to play important roles in micro-groove formation. Although the laser irradiation conditions must be optimized according to the thermophysical properties of the material, angled laser irradiation has the potential to effectively form micro-grooves.