Additively manufactured polymer structures often exhibit strong anisotropies due to their layered composition. Although existing methods in additive manufacturing (AM) for improving the mechanical properties are available, they usually do not eliminate the high degree of structural anisotropy. Existing methods for continuous fiber (cF) reinforcement in AM can significantly increase the mechanical properties in the strand direction, but often do not improve the interlaminar strength between the layers. In addition, it is mostly not possible to deposit cFs three-dimensionally and curved (variable–axial) and, thus, in a path that is suitable for the load case requirements. There is a need for AM methods and design approaches that enable cF reinforcements in a variable–axial way, independently of the AM mounting direction. Therefore, a novel two-stage method is proposed in which the process steps of AM and cF integration are decoupled from each other. This study presents the development and validation of the method. It was first investigated at the specimen level, where a significant improvement in the mechanical properties was achieved compared to unreinforced polymer structures. The Young’s modulus and tensile strength were increased by factors of 9.1 and 2.7, respectively. In addition, the design guidelines were derived based on sample structures, and the feasibility of the method was demonstrated on complex cantilevers.

This study focuses on a novel lightweight technology for manufacturing variable-axial fiber-reinforced polymer components. In the presented approach, channels following the load flow are implemented in an additively manufactured basic structure and impregnated continuous fiber bundles are pulled through these component-integrated cavities. Improved channel cross-section geometries to enhance the mechanical performance are proposed and evaluated. The hypothesis posits that increasing the surface area of the internal channels significantly reduces shear stresses between the polymer basic structure and the integrated continuous fiber composite. A series of experiments, including analytical, numerical, and microscopic analyses, were conducted to evaluate the mechanical properties of the composites formed, focusing on Young’s modulus and tensile strength. In addition, an important insight into the failure mechanism of the novel fiber composite is provided. The results demonstrate a clear correlation between the channel geometry and mechanical performance, indicating that optimized designs can effectively reduce shear stress, thus improving load-bearing capacities. The findings reveal that while fiber volume content influences the impregnation quality, an optimal balance must be achieved to enhance mechanical properties. This research contributes to the advancement of production technologies for lightweight components through additive manufacturing and the development of new types of composite materials applicable in various engineering fields.