The effect of a nonspherical particle shape and shape polydispersity on the structure of densely packed hard colloidal particles was studied in real space by confocal microscopy. We show that the first layer at the wall of concentrated size-monodisperse but shape-polydisperse polyhedral colloids exhibits significant deviations from a hexagonal lattice. These deviations are identified as bond-orientational fluctuations which lead to percolating “mismatch lines.” While the shape-induced geometrical frustration of the hexagonal symmetry suppresses translational order, bond-orientational order is clearly retained, indicating a hexaticlike structure of the polyhedral colloids.

For the preparation of electrically conductive composites, various combinations of cellulose and conducting materials such as polymers, metals, metal oxides and carbon have been reported. The conductivity of these cellulose composites reported to date ranges from 10⁻⁶ to 10³ S cm⁻¹. Cellulose nanocrystals (CNCs) are excellent building blocks for the production of high added value coatings. The essential process steps for preparing such coatings, i.e. surface modification of CNCs dispersed in water and/or alcohol followed by application of the dispersion to substrate samples using dip coating, are low cost and easily scalable. Here, we present coatings consisting of Ag modified CNCs that form a percolated network upon solvent evaporation. After photonic sintering, the resulting coatings are electrically conductive with an unprecedented high conductivity of 2.9 × 10⁴ S cm⁻¹. Furthermore, we report the first colloidal synthesis that yields CNCs with a high degree of Ag coverage on the surface, which is a prerequisite for obtaining coatings with high electrical conductivity.

Gelation is a common effect in aqueous suspensions of charged colloidal clay platelets at concentrations as low as 1 wt%. However, in systems of charged gibbsite [Al(OH)₃] platelets, gelation can be delayed to concentrations as high as 50 wt% depending on the ionic strength. We investigated the phase behaviour of this system approaching the state of gelation in the delicate region between attractive and repulsive states that originate from competition between Coulomb repulsion and van der Waals attraction. As a function of the ionic strength, isotropic–nematic, nematic–columnar and isotropic–columnar phase separations were observed. Moreover, compression by gravitational forces allowed us to observe phase separation that is arrested by gelation in the homogeneous suspensions.