The TiAlCrSiYN-based family of PVD (physical vapor deposition) hard coatings was specially designed for extreme conditions involving the dry ultra-performance machining of hardened tool steels. However, there is a strong potential for further advances in the wear performance of the coatings through improvements in their architecture. A few different coating architectures (monolayer, multilayer, bi-multilayer, bi-multilayer with increased number of alternating nano-layers) were studied in relation to cutting-tool life. Comprehensive characterization of the structure and properties of the coatings has been performed using XRD, SEM, TEM, micro-mechanical studies and tool-life evaluation. The wear performance was then related to the ability of the coating layer to exhibit minimal surface damage under operation, which is directly associated with the various micro-mechanical characteristics (such as hardness, elastic modulus and related characteristics; nano-impact; scratch test-based characteristics). The results presented exhibited that a substantial increase in tool life as well as improvement of the mechanical properties could be achieved through the architectural development of the coatings.

The TiAlCrSiYN-based family of physical vapor deposition (PVD) coatings were systematically designed through the incorporation of TiAlCrN interlayer to increase coating adhesion and consequently the tool life for extreme conditions that arise during dry high-speed milling of hardened tool steels. The investigation in the present paper intends to explain the effect of TiAlCrN interlayer thickness on the overall coating properties and cutting performance. A comprehensive characterization of the structure and properties of the coatings has been performed using focused ion beam (FIB), scanning electron microscope (SEM), X-ray powder diffraction (XRD), nanoindentation, ramped load scratch test, repetitive load wear test, and nano-impact test. The wear test at a subcritical load of 1.5 N showed that there was a gradual improvement in coating adhesion to the substrate as the interlayer thickness increased from 100 to 500 nm. However, the wear performance, being related to the ability of the coating layer to exhibit minimal surface damage under operation, was found to be associated with micro-mechanical characteristics (such as hardness, elastic modulus). Around a 40% increase in the cutting performance with 300 nm interlayer exhibited that a substantial increase in tool life can be achieved through interlayer thickness variation, by obtaining a balance between mechanical and tribological properties of the studied coatings.