A new family of physical vapor deposited (PVD) coatings is presented in this paper. These coatings are deposited by a superfine cathode (SFC) using the arc method. They combine a smooth surface, high hardness, and low residual stresses. This allows the production of PVD coatings as thick as 15 µm. In some applications, in particular for machining of such hard to cut material as compacted graphite iron (CGI), such coatings have shown better tool life compared to the conventional PVD coatings that have a lower thickness in the range of up to 5 μm. Finite element modeling of the temperature/stress profiles was done for the SFC coatings to present the temperature/stress profiles during cutting. Comprehensive characterization of the coatings was performed using XRD, TEM, SEM/EDS studies, nano-hardness, nano-impact measurements, and residual stress measurements. Application of the coating with this set of characteristics reduces the intensity of buildup edge formation during turning of CGI, leading to longer tool life. Optimization of the TiAlN-based coatings composition (Ti/Al ratio), architecture (mono vs. multilayer), and thickness were performed. Application of the optimized coating resulted in a 40–60% improvement in the cutting tool life under finishing turning of CGI.

The TiAlCrSiYN-based family of PVD (physical vapor deposition) hard coatings was specially designed for extreme conditions involving the dry ultra-performance machining of hardened tool steels. However, there is a strong potential for further advances in the wear performance of the coatings through improvements in their architecture. A few different coating architectures (monolayer, multilayer, bi-multilayer, bi-multilayer with increased number of alternating nano-layers) were studied in relation to cutting-tool life. Comprehensive characterization of the structure and properties of the coatings has been performed using XRD, SEM, TEM, micro-mechanical studies and tool-life evaluation. The wear performance was then related to the ability of the coating layer to exhibit minimal surface damage under operation, which is directly associated with the various micro-mechanical characteristics (such as hardness, elastic modulus and related characteristics; nano-impact; scratch test-based characteristics). The results presented exhibited that a substantial increase in tool life as well as improvement of the mechanical properties could be achieved through the architectural development of the coatings.

The TiAlCrSiYN-based family of physical vapor deposition (PVD) coatings were systematically designed through the incorporation of TiAlCrN interlayer to increase coating adhesion and consequently the tool life for extreme conditions that arise during dry high-speed milling of hardened tool steels. The investigation in the present paper intends to explain the effect of TiAlCrN interlayer thickness on the overall coating properties and cutting performance. A comprehensive characterization of the structure and properties of the coatings has been performed using focused ion beam (FIB), scanning electron microscope (SEM), X-ray powder diffraction (XRD), nanoindentation, ramped load scratch test, repetitive load wear test, and nano-impact test. The wear test at a subcritical load of 1.5 N showed that there was a gradual improvement in coating adhesion to the substrate as the interlayer thickness increased from 100 to 500 nm. However, the wear performance, being related to the ability of the coating layer to exhibit minimal surface damage under operation, was found to be associated with micro-mechanical characteristics (such as hardness, elastic modulus). Around a 40% increase in the cutting performance with 300 nm interlayer exhibited that a substantial increase in tool life can be achieved through interlayer thickness variation, by obtaining a balance between mechanical and tribological properties of the studied coatings.

Experimental investigations of nano-scale spatio-temporal effects that occur on the friction surface under extreme tribological stimuli, in combination with thermodynamic modeling of the self-organization process, are presented in this paper. The study was performed on adaptive PVD (physical vapor deposited) coatings represented by the TiAlCrSiYN/TiAlCrN nano-multilayer PVD coating. A detailed analysis of the worn surface was conducted using scanning electron microscopy and energy dispersive spectroscopy (SEM/EDS), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and Auger electron spectroscopy (AES) methods. It was demonstrated that the coating studied exhibits a very fast adaptive response to the extreme external stimuli through the formation of an increased amount of protective surface tribo-films at the very beginning of the running-in stage of wear. Analysis performed on the friction surface indicates that all of the tribo-film formation processes occur in the nanoscopic scale. The tribo-films form as thermal barrier tribo-ceramics with a complex composition and very low thermal conductivity under high operating temperatures, thus demonstrating reduced friction which results in low cutting forces and wear values. This process presents an opportunity for the surface layer to attain a strong non-equilibrium state. This leads to the stabilization of the exchanging interactions between the tool and environment at a low wear level. This effect is the consequence of the synergistic behavior of complex matter represented by the dynamically formed nano-scale tribo-film layer.

Zn _0.80 Cd _0.20 O/Zn _0.92 Cd _0.08 O multiple quantum-well (MQW) light-emitting diodes (LEDs) on p -type 4H-SiC substrates, using remote-plasma-enhanced metal-organic chemical vapor deposition, have been fabricated and characterized. Band-edge green electroluminescence (EL) at 500 nm has been obtained. The ZnCdO MQW LEDs show a rectifying current-voltage behavior with a turn-on voltage of 6.0 V. The integrated EL intensity linearly increases with increasing injection current density up to 1.9 A/cm ² . Furthermore, the presence of an EL blue-shift of 20 nm with increasing current and a large EL spectral width in comparison to PL are discussed in terms of Cd compositional fluctuations.