The photocatalytic activity of TiO₂ depends on numerous factors, such as the chemical potential of electrons, charge transport properties, band-gap energy, and concentration of surface-active sites. A lot of research has been dedicated to determining the properties that have the most significant influence on the photocatalytic activity of semiconductors. Here, we demonstrated that the activity of TiO₂ in the gas-phase reduction of CO₂ is governed mainly by the desorption rate of the reaction intermediates and final products. This indicates that the specific surface area of TiO₂ and binding strength of reaction intermediates and products are the main factors affecting the photocatalytic activity of TiO₂ in the investigated process. Additionally, it was shown that rutile exhibits higher photocatalytic activity than anatase/rutile mixtures mainly due to its high efficiency in the visible portion of the electromagnetic spectrum.

This study demonstrates the ability to control the properties of TiO₂–CuO_x composite layers for photocatalytic applications by using a simple electrophoretic deposition method from isopropanol-based suspension. To obtain uniform layers with a controlled composition, the surfactant sodium lauryl sulfate was used, which influenced the electrophoretic mobility of the particles and the morphology of the deposited layers. The TiO₂–CuO_x composite layers with different CuO_x contents (1.5, 5.5, and 11 wt.%) were obtained. It is shown that the optical band gap measured by UV–VIS–NIR diffuse reflectance spectra. When CuO_x is added to TiO₂, two absorption edges corresponding to TiO₂ and CuO_x are observed, indicating a broadening of the photosensitivity range of the material relative to pure TiO₂. An open-circuit potential study shows that by changing the amount of CuOx in the composite material, one can control the ratio of free charge carriers (n and p) and, therefore, the catalytic properties of the material. As a result, the TiO₂–CuO_x composite layers have enhanced photocatalytic activity compared to the pure TiO₂ layer: methanol yield grows with increasing CuO_x content during CO₂ photoreduction.

The present study investigates the photocatalytic properties of hydrothermally synthesized TiO₂ nanowires (NWs) for CO₂ reduction in H₂O vapor. It has been demonstrated that TiO₂ NWs, thermally treated at 500–700 °C, demonstrate an almost tenfold higher yield of products compared to the known commercial powder TiO₂ P25. It has been found that the best material is a combination of anatase, TiO₂-B and rutile. The product yield increases with increasing heat treatment temperature of TiO₂ NWs. This is associated with an increase in the degree of crystallinity of the material. It is shown that the best product yield of the CO₂ reduction in H₂O vapor is achieved when the TiO₂ NW photocatalyst is heated to 100 °C.

В данной работе представлено модифицирование ИК-излучателя на основе Ni-микронагревателей различной конфигурации слоем из смеси оксидов марганца. Показана методика получения смеси оксидов и формирование модифицирующего слоя на поверхности микронагревателя. В результате продемонстрировано увеличение равномерности разогрева микронагревателя и энергоэф- фективности в четыре раза. Результаты работы могут быть использованы для дальнейшего изготовления ИК-излучателей с повышенной эффективностью излучения.

В данной работе приводиться исследование фотокаталитической активности наноинтей TiO2, прошедших отжиг при различной температуре. Фотокаталитическая активность исследовалась путём восстановления CO2 до метана и метанола. Для получения нанонитей TiO2 использовался гидротермальный метод синтеза. Полученные нанонити имели длину порядка 8 мкм и диаметр 330 нм. После синтеза нанонити проходили отжиг при температурах 500, 700 и 900 °С. С увеличением температуры синтеза наблюдалось уменьшение ширины запрещённой зоны.

В работе путем варьирования технологических параметров процесса магнетронного осаждения при одновременном распылении двух мишеней получены тонкопленочные излучающие покрытия на основе силицида молибдена (MoXSiY) с различным стехиометрическим соотношением Mo0,2Si0,8, Mo0,3Si0,7 и Mo0,5Si0,5. Толщина осажденных пленок варьировалась в диапазоне от 150 до 500 нм. Проведены исследования темпера- турной стабильности, а также излучательной способности полученных покрытий при температуре нагрева до 600 °С. Наилучшая стойкость к окислению достигается для пленок состава Mo0,2Si0,8. В дальнейшем при- менение Mo0,2Si0,8 при создании МЭМС ИК-излучателей позволит повысить излучательную способность и ста- бильность устройств.