A new solar furnace has been designed and built at Plataforma Solar de Almería. In this work, its main components such as heliostat, concentrator, attenuator and test table, and the method used to align them are described. Other equipment like the auxiliary systems necessary for the solar operation, vacuum chamber and gas system are outlined too. Finally, the thermal characteristics of the focus were measured during a test campaign, where different planes along the optical axis were scanned with a radiometer, and the peak flux was obtained and is presented in the last section of this report.

This paper presents a procedure for making facetted mirrors to use in linear Fresnel reflectors, considering the design of the transversal geometry, materials, and structure configuration. Four different assemblies of the structure that supports and shapes the mirror are documented and evaluated. An assembly that implies a curved, pleated aluminum rectangular plate with a thin silvered-glass mirror vacuum glued to the plate is defined as the optimal. The geometrical quality of the chosen mirror facet’s configuration is accomplished by photogrammetry.

Thermal desorption, by a rotary kiln of mercury contaminated soil and mine wastes, has been used in order to volatilize mercury from the contaminated medium. Solar thermal desorption is an innovative treatment that uses solar energy to increase the volatility of contaminants, which are removed from a solid matrix by a controlled air flow system. Samples of soils and mine wastes used in the experiments were collected in the abandoned Valle del Azogue mine (SE, Spain), where a complex ore, composed mainly of cinnabar, arsenic minerals (realgar and orpiment) and stibnite, was mined. The results showed that thermal treatment at temperatures >400 °C successfully lowered the Hg content (2070–116 ppm) to 99%) were associated with the presence of significant contents of cinnabar and an equivalent diameter above 0.8 mm.

A novel approach for manufacturing porous materials, foreseen as solar receivers for concentrated sun radiation, used in the power tower technology is presented. In such applications, materials are subjected to steep thermal gradients and thousands of cycles. Yet, materials consisting of honeycombs and ceramic foams showed insufficient thermal performance. By using the fused filament fabrication process, one can design printed parts meeting the requirements for solar receivers, namely dark color and high solar absorptance. This exploratory study unveils data on the retained crushing strength of newly developed 3D-printed porous Black Zirconia cubes after thermal cycling under similar conditions to those experienced by volumetric receivers and catalyst substrates for solar fuels (H₂ and/or CO) production via the thermochemical cycle. Unlike dense ceramics, the resistance to thermal shock of 3D-printed cubes underwent a gradual decrease with the increase in the thermal gradient. The thermal shock cycles were performed between 800 °C and 1100, 1200, and 1300 °C, corresponding to a ΔT of 300, 400, and 500 K, respectively. Additionally, water quenching tests were performed at ΔT = 300 K up to 400 K. Crushing strength measurements carried out to evaluate the retained mechanical strength after exposure up to 100 cycles showed that the Black Zirconia cubes can withstand thermal gradients up to at least 400 K.