Screen-printed electrodes-based sensors can be successfully used to determine all kinds of analytes with great precision and specificity. However, obtaining a high-quality sensor can be difficult due to factors such as lack of reproducibility, surface contamination or other manufacturing challenges. An important step in ensuring reproducible results is the cleaning step. The aim of the current work is to help researchers around the world who struggle with finding the most suitable method for cleaning screen-printed electrodes. We evaluated the cleaning efficiency of different chemical compounds and cleaning methods using cyclic voltammetry and electrochemical impedance spectroscopy. The percentage differences in polarization resistance (Rp) before and after cleaning were as follows: acetone—35.33% for gold and 49.94 for platinum; ethanol—44.50% for gold and 81.68% for platinum; H₂O₂—47.34% for gold and 92.78% for platinum; electrochemical method—3.70% for gold and 67.96% for platinum. Thus, we concluded that all the evaluated cleaning methods seem to improve the surface of both gold and platinum electrodes; however, the most important reduction in the polarization resistance (R_p) was obtained after treating them with a solution of H₂O₂ and multiple CV cycles with a low scanning speed (10 mV/s).

In the current study, ZnO nanoparticles were obtained using a chemical process employing zinc acetate as the precursor, followed by thermal processing in air. To prevent agglomeration and increase the stability of ZnO nanoparticles, two unsaturated acids (e.g., elaidic acid and linoleic acid) and two saturated acids (e.g., stearic acid and lauric acid) were selected as capping agents. ZnO nanoparticles were investigated before and after surface modification with different fatty acids. Structural and morphological analyses of the samples were performed using FTIR and RAMAN spectroscopy, X-ray diffraction, SEM microscopy, and wetting capacity. Characterization studies revealed that the synthesized ZnO nanoparticles present well-defined crystalline structures, with crystallite sizes varying between 26 and 28 nm, and the average particle size was in the range of 10–55 nm (depending on the type of fatty acids used). The goniometric analysis followed the wetting capacity of the sample surface. The study results reveal that the capping agents have a considerable impact on the surface modification of the nanoparticles by increasing the contact angle. By producing nanoparticles with hydrophobic behavior, there is the possibility of opening up future research for their use in various applications across many industrial fields.

We report the relative humidity (RH) sensing response of a resistive sensor, employing sensing layers, based on a quaternary organic–inorganic hybrid nanocomposite comprising oxidized carbon nanohorns (CNHox), graphene oxide (GO), tin dioxide, and polyvinylpyrrolidone (PVP), at 1/1/1/1 and 0.75/0.75/1/1/1 mass ratios. The sensing structure comprises a silicon substrate, a SiO₂ layer, and interdigitated transducer (IDT) electrodes. The sensing film was deposited via the drop-casting method on the sensing structure. The morphology and the composition of the sensing layers were investigated through Scanning Electron Microscopy (SEM), X-ray diffraction (XRD), and RAMAN spectroscopy. The organic–inorganic quaternary hybrid-based thin film’s resistance increased when the sensors were exposed to relative humidity ranging from 0 to 100%. The manufactured devices show a room temperature response comparable to that of a commercial capacitive humidity sensor and characterized by excellent linearity, rapid response and recovery times, and good sensitivity. While the sensor with CNHox/GO/SnO₂/PVP at 0.75/0.75/1/1 as the sensing layer has the best performance in terms of linearity and recovery time, the structures employing the CNHox/GO/SnO₂/PVP at 1/1/1/1 (mass ratio) have a better performance in terms of relative sensitivity. We explained each constituent of the quaternary hybrid nanocomposites’ sensing role based on their chemical and physical properties, and mutual interactions. Different alternative mechanisms were taken into consideration and discussed. Based on the sensing results, we presume that the effect of the p-type semiconductor behavior of CNHox and GO, correlated with swelling of PVP, dominates and leads to the overall increasing resistance of the sensing layer. The hard–soft acid–base (HSAB) principle also supports this mechanism.

The study and discovery of bioactive compounds and new formulations as potential tools for promoting the repair of dermoepidermal tissue in wound healing is of continuing interest. We have developed a new formulation of amorphous hydrogel based on sodium alginate (NaAlg); type I collagen, isolated by the authors from silver carp tails (COL); glycerol (Gli); Aloe vera gel powder (AV); and silver nanoparticles obtained by green synthesis with aqueous Cinnamomum verum extract (AgNPs@CIN) and vitamin C, respectively. The gel texture of the amorphous hydrogels was achieved by the addition of Aloe vera, demonstrated by a rheological analysis. The evaluations of the cytotoxicity and cell proliferation capacity of the experimental amorphous hydrogels were performed against human foreskin fibroblast Hs27 cells (CRL-1634-ATCC). The developed gel formulations did not show a cytotoxic effect. The hydrogel variant containing AgNPs@CIN in a concentration of 8 µg Ag/gel formulation and hydrogel variant with vitamin C had proliferative activity. In addition, the antibacterial activity of the hydrogels was evaluated against S. aureus ATCC 6538, Ps. aeruginosa ATCC 27853, and E. coli ATCC 25922. The results demonstrated that the gel variant based on AgNPs@CIN in a concentration of 95 µg Ag/gel formulation and the hydrogel based on vitamin C show antibacterial activity. Therefore, the developed hydrogels with AgNPs@CIN and vitamin C could be promising alternatives in wound healing.

In this study we analyzed the structure and light-sensing properties of as-deposited vanadium oxide thin films, prepared by RF sputtering in different Ar:O₂ flow rate conditions, at low temperature (e.g., 65 °C). X-ray diffraction (XRD), Scanning Electron Microscopy (SEM-EDX), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) were employed to analyze the film microstructure, composition and the oxidation states of vanadium ions. The SEM micrographs evidence V_xO_y films with smooth surfaces, whereas the XRD patterns show their amorphous structure. Raman spectra indicate an increased structural disorder in the films deposited in Ar:O₂ flow comparatively with those deposited solely in Ar flow. The XPS data suggest the modification of the oxidation state from V⁴⁺ to V⁵⁺, thus proving the formation of the V₂O₅ phase when increasing the oxygen content, which further affects the films’ optical properties. We observed a good stability of the photogenerated current in Si/SiO₂/V_xO_y/TiN heterostructures upon excitation with pulses of UV (360 nm), VIS (white light) and NIR (860 nm) light. The responsivity, detectivity and linear dynamic range parameters increase with the O/V ratio in the V_xO_y films, reaching comparable values with photodetectors based on crystalline V₂O₅ or VO₂.

This paper presents the relative humidity (RH) sensing response of a resistive sensor employing sensing layers based on a ternary nanocomposite comprising graphene oxide-oxidized carbon nanohorns-polyvinylpyrrolidone (GO-CNHox–PVP), at 1/1/1, 1/2/1, and 1/3/1 w/w/w mass ratios. The sensing structure is composed of a silicon substrate, a SiO₂ layer, and interdigitated transducers (IDT) electrodes, on which the sensing layer is deposited via the drop-casting method. The morphology and the composition of the sensing layers are investigated through scanning electron microscopy (SEM) and RAMAN spectroscopy. The RH sensing capability of each carbonaceous nanocomposite-based thin film was analyzed by applying a current between the two electrodes and by measuring the voltage difference when varying the RH from 0% to 100% in humid nitrogen. The sensors have a room temperature response comparable to that of a commercial humidity sensor and are characterized by a rapid response, excellent linearity, good sensitivity, and recovery time. The manufactured sensing devices’ transfer functions were established, and we extracted the response and recovery times. While the structures with GO/CNHox/PVP at 1/1/1 ratio (w/w/w) had the best performance in terms of relative sensibility, response time, and recovery time, the sensors employing the GO/CNHox/PVP nanocomposite at the 1/2/1 ratio (w/w/w) had the best linearity. Moreover, the ternary mixture proved to have much better sensing properties compared to CNHox and CNHox-PVP-based sensing layers in terms of sensitivity and linearity. Each component of the ternary nanocomposites’ functional role is explained based on their physical and chemical properties. We analyzed the potential mechanism associated with the sensors’ response; among these, the effect of the p-type semiconductor behavior of CNHox and GO, correlated with swelling of the PVP, was dominant and led to increased resistance of the sensing layer.