Members of oral bacterial communities form biofilms not only on tooth surfaces but also on the surface of dental implants that replace natural teeth. Prolonged interaction of host cells with biofilm-forming anaerobes frequently elicits peri-implantitis, a destructive inflammatory disease accompanied by alveolar bone loss leading to implant failure. Here we wish to overview how the deposition of bioactive peptides to dental implant surfaces could potentially inhibit bacterial colonization and the development of peri-implantisis. One preventive strategy is based on natural antimicrobial peptides (AMPs) immobilized on titanium surfaces. AMPs are capable to destroy both Gram positive and Gram negative bacteria directly. An alternative strategy aims at coating implant surfaces - especially the transmucosal part - with peptides facilitating the attachment of gingival epithelial cells and connective tissue cells. These cells produce AMPs and may form a soft tissue seal that prevents oral bacteria from accessing the apical part of the osseointegrated implant. Because a wide variety of titanium-bound peptides were studied in vitro, we wish to concentrate on bioactive peptides of human origin and some of their derivatives. Furthermore, special attention will be given to peptides effective under in vivo test conditions.

Dental implants are artificial dental roots anchoring prosthetic restorations to replace natural teeth. Dental implant systems may have different tapered conical connections. Our research focused on the mechanical examination of implant–superstructure connections. Thirty-five samples with 5 different cone angles (24°, 35°, 55°, 75°, and 90°) were tested for static and dynamic loads, carried out by a mechanical fatigue testing machine. Fixing screws were fixed with a torque of 35 Ncm before measurements. For static loading, samples were loaded with a force of 500 N in 20 s. For dynamic loading, the samples were loaded for 15,000 cycles with a force of 250 ± 150 N. In both cases, the compression resulting from load and reverse torque was examined. At the highest compression load of the static tests, a significant difference (p = 0.021) was found for each cone angle group. Following dynamic loading, significant differences (p < 0.001) for the reverse torques of the fixing screw were also shown. Static and dynamic results showed a similar trend: under the same loading conditions, changing the cone angle—which determines the relationship between the implant and the abutment—had led to significant differences in the loosening of the fixing screw. In conclusion, the greater the angle of the implant–superstructure connection, the smaller the screw loosening due to loading, which may have considerable effects on the long-term, safe operation of the dental prosthesis.

The adhesion of biomolecules to dental and orthopedic implants is a fundamental step in the process of osseointegration. Short peptide motifs, such as RGD or KRSR, carried by extracellular matrix proteins or coated onto implant surfaces, accelerate cell adhesion and tissue formation. For this reason, understanding the binding mechanisms of adhesive peptides to oxidized surfaces of titanium implants is of paramount importance. We performed molecular dynamics simulations to compare the adhesion properties of 6 peptides, including the tripeptide RGD, its variants KGD and LGD, as well as the tetrapeptide KRSR, its variant LRSR and its truncated version RSR, on anatase, rutile, and amorphous titanium dioxide (TiO₂) surfaces. The migration of these molecules from the water phase to the surface was simulated in an aqueous environment. Based on these simulations, we calculated the residence time of each peptide bound to the three different TiO₂ structures. It was found that the presence of an N-terminal lysine or arginine amino acid residue resulted in more efficient surface binding. A pulling simulation was performed to detach the adhered molecules. The maximum pulling force and the binding energy were determined from the results of these simulations. The tri- and tetrapeptides had slightly greater adhesion affinity to the amorphous and anatase structure than to rutile in general, however specific surface and peptide binding characters could be detected. The binding energies obtained from our simulations allowed us to rank the adhesion strengths of the studied peptides.

Background: In this research the biomechanical properties of a bone model was examined. Porcine ribs are used as experimental model. The objective of this research was to investigate and compare the biomechanical properties of the bone model before and after implant placement. Methods: The bone samples were divided in three groups, Group 1 where ALL-ON-FOUR protocol was used during pre-drilling and placing the implants, Group 2 where ALL-ON-FOUR protocol was used during pre-drilling, and implants were not placed, and Group 3 consisting of intact bones served as a control group. Static and dynamic loading was applied for examining the model samples. Kruskal–Wallis statistical test and as a post-hoc test Mann–Whitney U test was performed to analyze experimental results. Results: According to the results of the static loading, there was no significant difference between the implanted and original ribs, however, the toughness values of the bones decreased largely on account of predrilling the bones. The analysis of dynamic fatigue measurements by Kruskal–Wallis test showed significant differences between the intact and predrilled bones. Conclusion: The pre-drilled bone was much weaker in both static and dynamic tests than the natural or implanted specimens. According to the results of the dynamic tests and after a certain loading cycle the implanted samples behaved the same way as the control samples, which suggests that implantation have stabilized the skeletal bone structure.

Due to its tensile strength and excellent biocompatibility, titanium (Ti) is commonly used as an implant material in medicine and dentistry. The success of dental implants depends on the formation of a contact between the oxidized surface of Ti implant and the surrounding bone tissue. The adsorption of proteins and peptides to the implant surface allows the bone-forming osteoblast cells to adhere to such modified surfaces. Recently, it has been observed that tetrapeptide KRSR (Lys-Arg-Ser-Arg) functionalization could promote osteoblast adhesion to implant surfaces. This may facilitate the establishment of an efficient bone-to implant contact and improve implant stability during the healing process. GROMACS, a molecular dynamics software package was used to perform a 200 ns simulation of adsorption of the KRSR peptide to the TiO₂ (anatase) surface in an aqueous environment. The molecule conformations were mapped with Replica Exchange Molecular Dynamics (REMD) simulations to assess the possible peptide conformations on the anatase surface, and the umbrella sampling method was used to calculate the binding energy of the most common conformation. The simulations have shown that the KRSR peptide migrates and attaches to the surface in a stable position. The dominant amino acid residue interacting with the TiO₂ surface was the N-terminal charged lysine (K) residue. REMD indicated that there is a distinct conformation that is taken by the KRSR peptide. In this conformation the surface interacts only with the lysine residue while the ser (S) and arg (R) residues interact with water molecules farther from the surface. The binding free energy of the most common conformation of KRSR peptide to the anatase (100) surface was ΔG = −8.817 kcal/mol. Our result suggests that the N-terminal lysine residue plays an important role in the adhesion of KRSR to the TiO₂ surface and may influence the osseointegration of dental implants.

This study aimed to evaluate the nanomechanical surface properties and water uptake of a flowable short-fiber-reinforced composite (SFRC) using various restorative techniques in order to assess its potential as a standalone restorative material. Nanoindentation and compressive creep testing were employed to characterize material performance. Three resin composites were examined: a flowable SFRC (everX Flow), a bulk-fill particulate filler composite (PFC), and a conventional PFC. Five experimental groups were established based on the restorative technique: layered PFC, layered SFRC, bulk SFRC, bulk PFC, and a bi-structure combining SFRC and PFC. Ninety standardized specimens (n = 18/group) were fabricated. Static and creep nanoindentation tests were conducted to assess surface properties, and water uptake was measured over a 30-day period. Data were analyzed using one-way ANOVA and Bonferroni post hoc tests. Nanoindentation revealed significant differences in hardness, with bulk PFC exhibiting the lowest values (p < 0.001). Creep testing indicated changes in modulus and viscosity following water storage. Notably, bulk SFRC showed the lowest water absorption (p < 0.001). Overall, bulk-applied SFRC demonstrated favorable nanomechanical properties and reduced water uptake, demonstrating its suitability as a standalone restorative material. Further clinical investigations are recommended to validate its long-term performance.