The main research objective of this study was to investigate the effect of the impregnation of Twaron® fabric with various shear thickening fluids (STFs) on the stab resistance at quasi-static conditions—being the main parameter characterizing the future application of the impregnated textiles in the scope of the new functionality of the elaborated protection of the multi-layer system. It was found that the STF/Twaron® fabric composites required significantly higher loading than the untreated fabric to achieve spike penetration. In the composite fabric tests, the spike did not fully puncture the material.

This paper describes studies on the surface modification of so-called ballistic materials (materials commonly used to protect the human body against firearms, i.e. fragments or bullets). Two materials, an ultra-high molecular weight polyethylene (UHMWPE) composite and aramid fabric, were investigated. The surfaces of these fibrous materials were modified using plasma-assisted chemical vapor deposition (PACVD) to examine the effects of the modification on the material properties, which are important for designing ballistic protections. Accordingly, both the mechanical strength and water resistance of the modified materials were tested. The results clearly show the impact of the modification on both parameters.

Investigations are presented for the preparation of a model hemostatic dressing that would exhibit an adequate hemostatic capacity in injuries and surgical wounds, an antibacterial activity to prevent primary and secondary infections, and offer safety in use. The Hemoguard dressing has been designed as a powder prepared from the complex chitosan/alginate Na/Ca in the form of micro- and nano-fibrids. Useful antibacterial and hemostatic properties of Hemoguard, which would qualify the material as first aid dressing and a temporary protection of injury wounds in field conditions, were assessed. Biocompatibility of the dressing was confirmed by biological in vitro examinations.

Designing medical devices requires a wide range of verification steps for estimation of the performance and safety. Designing the research program needs a rational selection of appropriate testing methods (in preclinical and clinical studies) for determination of the risk of potential incompatibilities resulting in adverse events. The significance of the appropriate selection of the testing method is increased in advanced medical devices. The presented research considers the verification of the functional properties of recently developed topical haemostatic agents with the use of the chitosan/alginate fibrids, based on the previously elaborated risk analysis made according to the guidelines of the PN-EN-ISO 14971:2012 and PN-EN ISO 22442-1:2008 standards. The aim of this research was to verify the stability of the performance of the newly developed haemostatic agents during storage. The defined aim of the study arose from the thesis that the appropriate selection of raw materials and a new manner of reprocessing them enabled keeping the usability of the final product for at least two years.

The process of textile modification using Plasma Assisted Chemical Vapour Deposition (PACVD) results in significant changes in surface properties with high effectivity. However, the main problem of the above-mentioned modification is to obtain a stable modification effect during standard use and storage. The aim of the study was to determine the stability of structural properties of PACVD-modified para-aramid ballistic woven fabrics during accelerated ageing using temperature or simultaneously temperature and humidity as the accelerated ageing factors. For identification of potential changes in the textile surface modified by PACVD with deposition of the polymer formed based on tetradecafluorohexane, the ATR-FTIR and SEM/EDS techniques were applied. The PACVD-modified textiles showed insignificant changes in structural properties after accelerated ageing using the above-men -tioned ageing factors. This confirms the stability of the PACVD-resulted modification during simulated conditions of standard use.