The aim of this study is to develop a process to produce high-performance cement-based composites reinforced with flax nonwoven fabrics, analyzing the influence of the fabric structure—thickness and entanglement—on mechanical behavior under flexural and tensile loadings. For this purpose, composite with flax nonwoven fabrics with different thicknesses were first prepared and their cement infiltration was evaluated with backscattered electron (BSE) images. The nonwoven fabrics with the optimized thickness were then subjected to a water treatment to improve their stability to humid environments and the fiber-matrix adhesion. For a fixed thickness, the effect of the nonwoven entanglement on the mechanical behavior was evaluated under flexural and direct tension tests. The obtained results indicate that the flax nonwoven fabric reinforcement leads to cement composites with substantial enhancement of ductility.

This research analyzes the effects of different treatments on flax nonwoven (NW) fabrics which are intended for composite reinforcement. The treatments applied were of two different kinds: a wet/dry cycling which helps to stabilize the cellulosic fibers against humidity changes and plasma treatments with air, argon and ethylene gases considering different conditions and combinations, which produce variation on the chemical surface composition of the NWs. The resulting changes in the chemical surface composition, wetting properties, thermal stability and mechanical properties were determined. Variations in surface morphology could be observed by scanning electron microscopy (SEM). The results of the X-ray photoelectron spectroscopy (XPS) showed significant changes to the surface chemistry for the samples treated with argon or air (with more content on polar groups on the surface) and ethylene plasma (with less content of polar groups). Although only slight differences were found in moisture regain and water retention values (WRV), significant changes were found on the contact angle values, thus revealing hydrophilicity for the air-treated and argon-treated samples and hydrophobicity for the ethylene-treated ones. Moreover, for some of the treatments the mechanical testing revealed an increase of the NW breaking force.

With the substantial growth of the smart textiles market, electrical properties are becoming a basic requirement for most of the advanced textiles used in the development of wearable solutions and other textile-based smart applications. Depending on the textile substrate, the test method to determine the electrical properties can be different. Unlike smart fibers and yarns, the characterization of the electrical properties of fabrics cannot be tested between two connection points because the result would not represent the behavior of the entire fabric, so the electrical properties must be related to an area. The parameters used to characterize the electrical properties of the fabrics include resistance, resistivity, and conductivity. Although all of them can be used to indicate electrical performance, there are significant differences between them and different methods available for their determination, whose suitability will depend on the function and the textile substrate. This paper revises the main parameters used to characterize the electrical properties of conductive fabrics and summarizes the most common methods used to test them. It also discusses the suitability of each method according to several intervening factors, such as the type of conductive fabric (intrinsically or extrinsically conductive), its conductivity range, other fabric parameters, or the final intended application. For intrinsically conductive woven fabrics, all the methods are suitable, but depending on the requirements of conductivity accuracy, the contact resistance from the measuring system should be determined. For intrinsically conductive knitted fabrics, two-point probe, Van der Pauw, and eddy current methods are the most suitable. And for intrinsically conductive nonwoven fabrics, two-point probe and four-point probe methods are the most appropriate. In the case of extrinsically conductive fabrics, the applied method should depend on the substrate and the properties of the conductive layer.

The aim of this study is to propose and explore a novel approach for the production of cellular lightweight natural fibre, nonwoven, fabric-reinforced biocomposites by means of gas dissolution foaming from composite precursors of polyhydroxybutyrate-based matrix and flax fabric reinforcement. The main challenge is the development of a regular cellular structure in the polymeric matrix to reach a weight reduction while keeping a good fibre-matrix stress transfer and adhesion. The viability of the process is evaluated through the analysis of the cellular structure and morphology of the composites. The effect of matrix modification, nonwoven treatment, expansion temperature, and expansion pressure on the density and cellular structure of the cellular composites is evaluated. It was found that the nonwoven fabric plays a key role in the formation of a uniform cellular morphology, although limiting the maximum expansion ratio of the composites. Cellular composites with a significant reduction of weight (relative densities in the range 0.4–0.5) were successfully obtained.

In this paper, a full textile capacitive woven sensor integrated over a textile substrate is presented. The sensor consists in an interdigitated capacitance prepared to measure moisture and/or presence detection. In order to evaluate the sensor response to moisture, capacitance has been measured by means of an LCR meter from 20 Hz to 20 kHz in a climatic chamber with a swept of the relative humidity (RH) from 30% to 90% at 20 °C. Subsequently, presence response is evaluated measuring the capacitance of the woven sensor meanwhile a person is sitting down and getting up. The woven sensor results demonstrate its functionality over moisture measurement where sensor capacitance changes from a minimum of 9.74 pF at 30% RH to a maximum of 2.31 uF at 90% RH. The presence detection is also demonstrated, which makes the capacitance variation change from a 10% of capacitance variation when the chair is empty, to a capacitance variation of 170% when a person is sitting on it. The adaptation of the weaving process to accomplish a fully integrated sensor provides a better repeatability than previous embroidered sensors and opens a door to being commercially produced.