Sequential extraction method was applied to lignins from hardwood and softwood isolated by kraft and VTT organosolv processes. Solvent extraction was found to fractionate lignin according to the molecular weight: small molecular weight lignin is dissolved in the organic solvents and the lignin with higher molecular weight is enriched into the residue. Isolated acetone fractions of lignin are more homogeneous with narrow molecular weight distributions. Based on the³¹P NMR results, both total hydroxyl content and the content of phenolic hydroxyl units are higher in the acetone fraction than in the residue. Pyrolysis-GC/MS of all lignins showed thatp-hydroxy phenols are enriched to the residues. Preferential dissolution of syringyl type lignin in acetone was observed for hardwood kraft lignin, whereas the opposite behavior was seen for the hardwood organosolv lignin. Glass transition temperatures of all acetone soluble fractions were notably low compared to starting and residue lignins, which gives possibilities for future applications as a material with specific properties.

Interest in biobased polymers from renewable resources has grown in recent years due to environmental concerns, but they still have a minimal fraction of the total global market. In this study, the injection molding of thermoplastic cellulose octanate (cellulose C8) and cellulose palmitate (cellulose C16) were studied. The mechanical properties of injection-molded test specimens were analyzed by using tensile testing, and the internal structure of injection-molded objects was studied by using a field emission scanning electron microscopy (FE-SEM). We showed that thermoplastic cellulose C8 and cellulose C16 were completely processable without the addition of a plasticizer, which is very unusual in the case of cellulose esters. The compatibility of cellulose esters with poly(lactic acid) (PLA) and biopolyethylene (bio-PE) was also tested. By compounding the cellulose esters with PLA, the elongation of PLA-based blends could be improved and the density could be reduced. The tested thermoplastic cellulose materials were fully biobased, and have good future potential to be used in injection molding applications.