This study deals with an investigation of how substitution of an alcohol group by a thiol group in mixtures of choline chloride with a series of bio-sourceable molecules affects the physico-chemical properties of the mixtures and their ability to dissolve metal oxides. All of the thiol mixtures studied showed a higher affinity and selectivity for late transition metals and the physical properties of the mixtures were improved compared to their alcohol analogues (i.e. lower viscosity, wider liquid range). The metal solubility was assessed via determination of the final concentration of the metal oxides dissolved in thiol mixtures via inductively coupled plasma optical emission spectroscopy (ICP-OES). The thiol function selectively improved the solubilities of the late transition metal oxides (i.e. copper and zinc), which are valuable metals often present as residue in industrial waste. The solubility of iron oxides was much lower than that of the valuable metals, which is a significant benefit in industrial applications. The different solubilization behaviour of metal oxides in the thiol and alcohol mixtures was further investigated via UV-vis absorption and infrared spectroscopy. This study allowed the potential of these deep-eutectic solvents for the selective recovery of metals to be assessed.

Interest in biobased polymers from renewable resources has grown in recent years due to environmental concerns, but they still have a minimal fraction of the total global market. In this study, the injection molding of thermoplastic cellulose octanate (cellulose C8) and cellulose palmitate (cellulose C16) were studied. The mechanical properties of injection-molded test specimens were analyzed by using tensile testing, and the internal structure of injection-molded objects was studied by using a field emission scanning electron microscopy (FE-SEM). We showed that thermoplastic cellulose C8 and cellulose C16 were completely processable without the addition of a plasticizer, which is very unusual in the case of cellulose esters. The compatibility of cellulose esters with poly(lactic acid) (PLA) and biopolyethylene (bio-PE) was also tested. By compounding the cellulose esters with PLA, the elongation of PLA-based blends could be improved and the density could be reduced. The tested thermoplastic cellulose materials were fully biobased, and have good future potential to be used in injection molding applications.

The increasing environmental awareness is driving towards novel sustainable high-performance materials applicable for future manufacturing technologies like additive manufacturing (AM). Cellulose is abundantly available renewable and sustainable raw material. This work focused on studying the properties of thermoplastic cellulose-based composites and their properties using injection molding and 3D printing of granules. The aim was to maximize the cellulose content in composites. Different compounds were prepared using cellulose acetate propionate (CAP) and commercial cellulose acetate propionate with plasticizer (CP) as polymer matrices, microcellulose (mc) and novel cellulose-ester additives; cellulose octanoate (C8) and cellulose palmitate (C16). The performance of compounds was compared to a commercial poly(lactic acid)-based cellulose fiber containing composite. As a result, CP-based compounds had tensile and Charpy impact strength properties comparable to commercial reference, but lower modulus. CP-compounds showed glass transition temperature (Tg) over 58% and heat distortion temperature (HDT) 12% higher compared to reference. CAP with C16 had HDT 82.1 °C. All the compounds were 3D printable using granular printing, but CAP compounds had challenges with printed layer adhesion. This study shows the potential to tailor thermoplastic cellulose-based composite materials, although more research is needed before obtaining all-cellulose 3D printable composite material with high-performance.

Technical and hygienic nonwovens, originating typically from fossil‐based synthetic polymers, are the fastest growing applications in the textile industry. Recently developed thermoplastic cellulose fatty acid esters have polyolefin like rheology properties and therefore the suitability of these cellulose esters for fiber production was evaluated. In this study, the melt spinning of textile fibers has been demonstrated using thermoplastic cellulose octanoate. The mechanical properties of melt spun fibers were analyzed by using tensile testing and both the surface and cross‐section morphology of melt spun fibers were studied using the scanning electron microscopy. The surfaces of the fibers were very smooth and also the cross‐section was very uniform and no porosity was observed. While mechanical properties of the produced fibers are not yet as good as those reported for commercial polypropylene (PP) monofilament fibers, they are somewhat more comparable to other cellulose ester‐based fibers. The melt spinning results indicate that the novel cellulose‐based fibers can provide a renewable and recyclable alternative, for example, spun‐laid PP in several hygienic textile and fully oriented in technical applications in future.

Polymer foams are widely used in several fields such as thermal insulation, acoustics, automotive, and packaging. The most widely used polymer foams are made of polyurethane, polystyrene, and polyethylene but environmental awareness is boosting interest towards alternative bio-based materials. In this study, the suitability of bio-based thermoplastic cellulose palmitate for extrusion foaming was studied. Isobutane, carbon dioxide (CO₂), and nitrogen (N₂) were tested as blowing agents in different concentrations. Each of them enabled cellulose palmitate foam formation. Isobutane foams exhibited the lowest density with the largest average cell size and nitrogen foams indicated most uniform cell morphology. The effect of die temperature on foamability was further studied with isobutane (3 wt%) as a blowing agent. Die temperature had a relatively low impact on foam density and the differences were mainly encountered with regard to surface quality and cell size distribution. This study demonstrates that cellulose palmitate can be foamed but to produce foams with greater quality, the material homogeneity needs to be improved and researched further.