Objective: The purpose of this study was to investigate and compare the crystalline structures of recently released MTA Plus (MTA-P), MTA Angelus (MTA-A), DiaRoot BioAggregate (BA) by X-ray diffraction (XRD) analysis. Materials and Methods: Phase analysis was carried out on powder and set forms of tested materials. The powder specimens placed into sample holders that were packed with a glass slide and the set samples prepared according to the manufacturer's instructions were placed into molds. The samples after being set for three days at 37°C and 100% humidity in an incubator were mounted onto the XRD machine and phase identification was accomplished using a search-match software program. Results: XRD findings indicated that major constituents of MTA-P were bismuth oxide, portlandite, dicalcium silicate and tricalcium silicate. The crystal structure of MTA-A were similar to those of MTA-P except for the absence of portlandite. Additionally, MTA-A had tricalcium aluminate differing from MTA-P. BA mainly differed from MTA-P and MTA-A by the radiopacifier (tantalum oxide-TO) in its composition. Conclusions: The majority of constituents of the tested materials have shown similarity except for the presence of tricalcium aluminate in MTA-A and the inclusion of TO in BA. In addition, set MTA-P showed a strong peak of portlandite.

Objective. The aim of this study was to evaluate and compare, both clinically and radiographically, the effects of calcium silicate-based materials (i.e., ProRoot MTA [PR-MTA], MTA-Plus [MTA-P], and Biodentine [BD]) and ferric sulfate [FS] in pulpotomy of primary molars. Materials and Methods. In this randomized clinical trial, 29 healthy 5- to 7-year-old children with at least four carious primary molars with no clinical or radiographic evidence of pulp degeneration were enrolled. The pulpotomy agents were assigned as follows: Group 1: BD; Group 2: MTA-P; Group 3: PR-MTA; and Group 4: FS. Clinical and radiographic evaluations were performed at 6, 12, and 24 months. Data were analyzed using chi-square tests. Results. Total success rates at 24 months were 82.75%, 86.2%, 93.1%, and 75.86%, respectively. No statistically significant differences in total success rates were observed among the groups at 6-, 12-, and 24-month follow-ups. When the groups were compared according to follow-up times, the success rates in each group did not vary significantly among the 6–12-month, 6–24-month, or 12–24-month periods (p>0.05). Conclusion. Although the success rates of BD, MTA-P, MTA-PR, and FS did not differ significantly, calcium silicate-based materials appeared to be more appropriate than FS in clinical practice.

İstanbul Üniversitesi | Tarihten Geleceğe Bilim Köprüsü- 1453

Amaç: Bu çalışmanın amacı Türk toplumunda dental anomali görülme sıklığının cinsiyet ve yaşa göre araştırılmasıdır.Gereç ve Yöntem: Çalışmada İstanbul Üniversitesi Diş Hekimliği Fakültesi Ağız, Diş-Çene Radyolojisi Anabilim Dalı’na başvuran, yaşları 9-35 yaş arasında değişen (ortalama yaş: 25.61±10.04) 2025 hastanın (885 erkek ve 1140 kadın) panoramik radyografileri geriye dönük olarak araştırılmıştır. Hastalar hipodonti, hiperdonti, mikrodonti, taurodontizm ve diğer kök anomalileri gibi dental anomalilerin varlığı açısından incelenmiştir. Bu anomalilerin görülme oranları cinsiyet ve yaşa göre değerlendirilmiştir.Bulgular: 2025 hastanın toplam 96’sının (42 erkek, 54 kadın) incelenen dental anomalilerden en az birine sahip olduğu belirlenmiştir (%4.74). en sık gözlenen dental anomali diş eksikliği olup (%1.77) bunu sırasıyla taurodontizm (%1.18), hiperdonti (%0.79), mikrodonti (%0.54) ve diğer kök anomalileri (%0.44) takip etmektedir.Sonuç: Diş eksikliği incelenen populasyonda en sık gözlenen gelişimsel dental anomali olup bunu taurodontizm takip etmektedir

Background: As calcium silicate-based cements (CSCs) have found success in various vital pulp therapy applications, several new CSC products have emerged. This study aimed to assess the genotoxicity, cytotoxicity, and bioactivity of four CSCs by comparing the newly introduced materials Bio MTA+ and MTA Cem with previously studied materials, Biodentine and NeoMTA. Methods: Genotoxicity was evaluated using the micronucleus (MN) assay in human peripheral blood lymphocyte cells, measuring MN frequency and nuclear division index (NDI). Cytotoxicity was assessed in human dental pulp stem cells through the Water-Soluble Tetrazolium Salt-1 (WST-1) colorimetric assay. Bioactivity was determined by ELISA, measuring the levels of angiogenic and odontogenic markers (BMP-2, FGF-2, VEGF, and ALP). Statistical analyses included ANOVA, Dunnet and Sidak tests, and Wald chi-square test. (p < .05). Results: The MN frequency in the groups was significantly lower than that in the positive control group (tetraconazole) (p < .05). NDI values decreased with increasing concentration (p < .05). Bio MTA+ and NeoMTA showed decreased cell viability at all concentrations in 7-day cultures (p < .01). All materials increased BMP-2, FGF-2, and VEGF levels, with Biodentine and NeoMTA showing the highest levels of BMP-2 and FGF-2 on day 7. Biodentine displayed the highest VEGF levels on day 7. Biodentine and NeoMTA groups exhibited significantly higher ALP activity than the Bio MTA+ and MTA Cem groups by day 7. Conclusion: Bio MTA+ and MTA Cem demonstrated no genotoxic or cytotoxic effects. Moreover, this study revealed bioactive potentials of Bio MTA+ and MTA Cem by enhancing the expression of angiogenic and osteogenic growth factors.

Objective The aim of this in vitro study was to assess the antimicrobial properties of newly formulated toothpastes (four toothpastes for adults and two toothpastes for kids/babies) and a mouthrinse. Materials and Methods Newly formulated six different toothpastes and one mouthrinse of a single brand and commercially available five toothpastes and three mouthrinse were investigated for their antimicrobial activity against two oral pathogens, Streptococcus mutans and Candida albicans, by agar well diffusion assay. After incubation, the inhibition zone diameters were measured in millimeters and statistical analyses were performed. Results All experimental adult toothpastes exhibited good antimicrobial activity against S. mutans and C. albicans except the experimental toothpaste D. Experimental toothpaste B exhibited the highest antibacterial activity against C. albicans and S. mutans. Experimental toothpaste for kids showed the best antimicrobial activity against S. mutans when kids’ toothpastes were compared. None of the tested toothpastes for kids/babies showed antibacterial effects for C. albicans. Among the mouthrinse tested, Sensodyne mouthrinse showed the best results. Experimental mouthrinse showed significantly lower antibacterial activity against S. mutans then Sensodyne, Eludril, and chlorhexidine mouthrinse. Conclusion Although experimental toothpaste and mouthrinse formulations revealed good results in terms of antimicrobial activity to some specific microorganisms, further studies involving more bacterial species or analyzing the quality and efficacy of these products by other in vitro or in vivo tests are needed.