The microstructure and texture evolution of cold-rolled low carbon steel after ultrafast heating and quenching is investigated. Experiments were carried out at heating rates of 150 °C/s and 1500 °C/s. The recrystallization of ferrite is studied by scanning electron microscopy and electron backscattered diffraction techniques. The texture evolution of cold rolled steel during ultrafast heating was studied, making it possible to estimate the precise effect of heating rate on the orientations of newly formed grains. The experimental results showed that the recrystallization of ferrite was not completed before the full transformation of austenite. The noticeable increase in the fraction of recrystallized grains of diameter less than 1 µm, when the heating rate is increased from 150 °C/s to 1500 °C/s suggests that the increase of the heating rate enhances the nucleation of ferrite. The crystallographic orientations in recrystallized ferrite are strongly influenced by the heating rates. The effect of heating rate in the releasing of stored energy, carbon diffusion and spheroidization of cementite might explain some differences in textures observed in recrystallized ferrite.

The effect of heating rate on the formation and decomposition of austenite was investigated on cold-rolled low carbon steel. Experiments were performed at two heating rates, 150 °C/s and 1500 °C/s, respectively. The microstructures were characterized by means of scanning electron microscopy (SEM) and electron backscattered diffraction (EBSD). Experimental evidence of nucleation of austenite in α/θ, as well as in α/α boundaries is analyzed from the thermodynamic point of view. The increase in the heating rates from 150 °C/s to 1500 °C/s has an impact on the morphology of austenite in the intercritical range. The effect of heating rate on the austenite formation mechanism is analyzed combining thermodynamic calculations and experimental data. The results provide indirect evidence of a transition in the mechanism of austenite formation, from carbon diffusion control to interface control mode. The resulting microstructure after the application of ultrafast heating rates is complex and consists of a mixture of ferrite with different morphologies, undissolved cementite, martensite, and retained austenite.