The effect of N content on the microstructure and wear resistance of 4Cr13 corrosion-resistant plastic mold steel were investigated by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and tribometer. The results showed that the influence mechanism of nitrogen on the hardness of the test steels responded to the changes in the quenching temperature. When the quenching temperature was below 1050 °C, the solid solution strengthening of N played a dominant role as a wear mechanism, and as the N content increased, the hardness of the steel increased. When the quenching temperature was higher than 1050 °C, N increased the residual austenite content, resulting in a decrease in hardness. The addition of N reduced the optimal quenching temperature of the test steels. The N addition promoted the transformation of large-sized M₂₃C₆ to M₂₃C₆ and fine Cr₂N, resulting in an increase in the hardness of the test steels. The influence on the wear resistance of the experimental steels differed according to the varied N contents. The addition of 0.1% N delayed the precipitation of large- sized particles in the second phase, increased the hardness of the steel, and reduced the degree of wear. However, an excessive addition of N (0.18%) led to the excessive precipitation of the second-phase particles, and the second-phase particles then gradually flaked during the wear process and continued to participate in the wear process as third-body abrasives, reducing wear resistance.

A novel non-magnetic Fe-21Cr-15Ni-5Mn-2Mo austenitic stainless steel with high strength and plasticity has been developed. The microstructure and liquid helium temperature (4.2 K) tensile properties of the top and bottom samples of large-size forged flat steel after solution treatment at 1090 °C were investigated. The results showed that the average grain size of the bottom sample (48.0 ± 6.7 μm) was smaller than that of the top sample (58.8 ± 15.3 μm), and the MX precipitates and Z phases were distributed in the matrix of the samples. The 4.2 K strengths of the samples at the top and bottom were high, and large amounts of annealing twin boundaries played a certain role in strengthening. After cryogenic tensile testing, large amounts of deformation twins, stacking faults, and dislocations were generated inside the austenite grains of both samples, which helped the material to obtain higher plasticity and strength. The top and bottom samples possessed excellent synergies of strength and plasticity at 4.2 K, and the 4.2 K tensile properties of the top sample were as follows: ultimate tensile strength (UTS) of 1850 MPa, yield strength (YS) of 1363 MPa, and elongation (EL) of 26%. The tested steel is thus believed to meet the requirements of combined excellent strength and plasticity within a deep cryogenic environment, and it would be a promising material candidate for manufacturing superconducting coil cases to serve in new generation fusion engineering.

This paper employs in situ Electron Backscatter Diffraction (EBSD) tensile technology to thoroughly consider the evolution of microstructure, grain size, grain boundary characteristics, orientation differences, and dislocation density of H13 steel during the elastic and plastic stages of room temperature tensile testing. The study unveils the deformation mechanisms of inclusions, carbides, and the matrix in H13 steel during the various stages, providing a comprehensive explanation for the slightly superior tensile properties of H13 steel when refined by Vacuum Induction Melting combined with Vacuum Arc Remelting (VIM + VAR) over those when refined by Electroslag Remelting (ESR). This discrepancy is primarily attributed to the differences in inclusions and carbides present in the two refining processes. The quantity and size of inclusions and carbides are closely related to material fracture. Large-sized carbides and inclusions were shown to be more likely to cause dislocation pile-ups and stress concentration. This, in turn, leads to faster crack initiation and propagation during plastic deformation. Conversely, the formation of micro-pores within these fine inclusions and the matrix is contingent on greater plastic deformation, resulting in a gradual and incremental linkage of these micro-pores to form dimples beneath the influence of slip.

As an advanced near-net-shape processing method in which directly preformed, semi-finished products are created from liquid metals, spray forming has become popular in the development and application of new materials and is supporting industrialization. However, as investigated in this work, the problems of segregation and low hardness exist in the actual industrialization process, particularly for large-diameter M3 high-speed steel. It was here found that the annual ring segregation morphologies were mostly distributed from the edge to 1/2R, with a large number of stripes primarily enriched in C, Mo, and Cr elements, and the degree of segregation was mild. The ring segregation was located at the 1/2R position, where the main elemental enrichments were C, W, Mo, Cr, and V, and the segregation degree was severe. The formation of segregation during deposition is described based on an equilibrium solidification model. A slow cooling rate and heat dissipation from the surface to the inside were judged to be the main factors causing segregation and changes in the carbide morphology. In terms of hardness, with the increase in the quenching temperature to 1230 °C, the tempering hardness increased significantly. The analysis shows that a faster cooling rate in the atomization stage caused the solidified droplets to exhibit rapid solidification characteristics, and there was a higher proportion of MC carbide in the deposited billet. MC carbides cannot be fully dissolved using the conventional heat treatment process, which decreases the C, Cr, Mo, and V contents in the solution and, thus, reduces the secondary hardening capability. The findings show that, when the spray forming process is used to prepare large-diameter materials, it should not be considered a rapid solidification technology simply because of its atomization stage. Moreover, more attention should be paid to the influence of microstructure transformation during atomization and deposition.

In this study, various testing methods, including X-ray diffraction (XRD), scanning electron microscopy (SEM), Electron Backscatter Diffraction (EBSD), and high-resolution transmission electron microscopy (HRTEM), were utilized to examine the effects of aging time on the microstructure and mechanical properties of ultra-high-strength heat-resistant bearing steel. The findings revealed that as the aging time progressed, the tensile strength, yield strength, and elongation exhibited an initial increase followed by a decline. Specifically, after 50 h of aging, the tensile strength and yield strength peaked at 2133 MPa and 1874 MPa, respectively. Calculations indicated that precipitation strengthening was the primary contributor to the strength, accounting for 1311 MPa. During the aging process, the martensite laths underwent coarsening, broadening from 202 nm to 306.5 nm, while the residual austenite remained relatively stable. Additionally, dislocations underwent annihilation, resulting in a decrease in dislocation density to 4.84 × 10¹¹/cm² at 100 h. As the aging time continued to increase, both M₆C and M₂C phases gradually coarsened. Notably, the number of M₂C phases increased, and they transformed from an acicular shape to a spherical shape at 100 h.