Composites based on epoxy/graphene oxide (GO) and epoxy/reduced graphene oxide (rGO) were investigated for thermal-mechanical performance focusing on the effects of the chemical groups present on nanoadditive-enhanced surfaces. GO and rGO obtained in the present study have been characterized by Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), and X-ray powder diffraction (XRD) demonstrating that materials with different oxidation degrees have been obtained. Thereafter, GO/epoxy and rGO/epoxy nanocomposites were successfully prepared and thoroughly characterized by dynamic mechanical thermal analysis (DMTA) and transmission electron microscopy (TEM). A significant increase in the glass transition temperature was found in comparison with the neat epoxy. The presence of functional groups on the graphene surface leads to chemical interactions between these functional groups on GO and rGO surfaces with the epoxy, contributing to the possible formation of covalent bonds between GO and rGO with the matrix. The presence of oxidation groups on GO also contributes to an improved exfoliation, intercalation, and distribution of the GO sheets in the composites with respect to the rGO based composites.

While most ferns avoid freezing as they have a tropical distribution or shed their fronds, wintergreen species in temperate and boreoalpine ecosystems have to deal with sub-zero temperatures. Increasing evidence has revealed overlapping mechanisms of desiccation and freezing tolerance in angiosperms, but the physiological mechanisms behind freezing tolerance in ferns are far from clear. We evaluated photochemical and hydraulic parameters in five wintergreen fern species differing in their ability to tolerate desiccation. We assessed frond freezing tolerance, ice nucleation temperature and propagation pattern, and xylem anatomical traits. Dynamics of photochemical performance and xanthophyll cycle were evaluated during freeze–thaw events under controlled conditions and, in selected species, in the field. Only desiccation-tolerant species, which possessed a greater fraction of narrow tracheids (<18 μm) than sensitive species, tolerated freezing. Frond freezing occurred in the field at –3.4 ± 0.9 °C (SD) irrespective of freezing tolerance, freezable water content, or tracheid properties. Even in complete darkness, maximal photochemical efficiency of photosystem II was down-regulated concomitantly with zeaxanthin accumulation in response to freezing. This was reversible upon re-warming only in tolerant species. Our results suggest that adaptation for freezing tolerance is associated with desiccation tolerance through complementary xylem properties (which may prevent risk of irreversible cavitation) and effective photoprotection mechanisms. The latter includes de-epoxidation of xanthophylls in darkness, a process evidenced for the first time directly in the field.

An innovative method to switch the wettability of a micropatterned polymeric surface by thermally induced shape memory effect is presented. For this purpose, first polycyclooctene (PCO) is crosslinked with dycumil peroxide (DCP) and its melting temperature, which corresponds with the switching transition temperature (Ttrans), is measured by Dynamic Mechanical Thermal Analysis (DMTA) in tension mode. Later, the shape memory behavior of the bulk material is analyzed under different experimental conditions employing a cyclic thermomechanical analysis (TMA). Finally, after creating shape memory micropillars by laser ablation of crosslinked thermo-active polycyclooctene (PCO), shape memory response and associated effect on water contact angle is analyzed. Thus, deformed micropillars cause lower contact angle on the surface from reduced roughness, but the original hydrophobicity is restored by thermally induced recovery of the original surface structure.

Delamination and brittle matrix fracture have long since been the biggest problems in fibre-reinforced composites. Recently, the incorporation of electrospun nanofibre veils has been shown to be an effective method for improving the mechanical properties of these composites, without causing process problems and negatively affecting other mechanical properties. Thus, these nanofibres have the potential to be used as thickness-reinforcing materials in composites. This paper investigates the effect of incorporating standalone electrospun nanofibre veils made of two different types of polyamide 6 (PA6) on the mechanical properties of carbon fibre/epoxy composites. The influence of positioning the electrospun veils at different interlaminar positions of the laminate has also been investigated.

The inclusion of electrospun nanofiber veils was revealed as an effective method for enhancing the mechanical properties of fiber-reinforced epoxy resin composites. These veils will eventually allow the incorporation of nanomaterials not only for mechanical reinforcement but also in multifunctional applications. Therefore, this paper investigates the effect of electrospun nanofibrous veils made of polyamide 6 modified with TiO₂ nanoparticles on the mechanical properties of a carbon-fiber/epoxy composite. The nanofibers were included in the carbon-fiber/epoxy composite as a single structure. The effect of positioning these veils in different composite positions was investigated. Compared to the reference, the use of unmodified and TiO₂ modified veils increased the flexural stress at failure and the fracture toughness of composites. When TiO₂ modified veils were incorporated, new antibacterial properties were achieved due to the photocatalytic properties of the veils, widening the application area of these composites.