In this paper, gas chromatography–mass spectrometry (GC–MS) and positron annihilation lifetime spectroscopy (PALS) were used to probe the changes of oligomers and the polydimethylsiloxane (PDMS) network in silicone rubber, after different durations of UVA/UVB irradiation. At the early stage (300 h) of UVB irradiation, D${}_4$ was generated and the lifetime of ${\tau }_3$ also increased, indicating the rupture of the Si-O bond in the PDMS network. These two aging processes were termed the post curing process and the chain session process. The new finding was that UVA could only induce the post curing process; UVB causes the rupture of the chemical bond in silicone rubber. Photons of UVB could break the C-H bond, and then trigger the backbiting decomposition of PDMS, breaking the Si-O bond, while the photons of UVA cannot. The fact that D${}_4$ was generated after UVB irradiation can be used to evaluate the UVB stability of silicone rubber in the future.

Silicone rubber is widely used as an insulating material. In this article, silicone rubber samples were prepared by varying the content of crosslinker (2,5-bis(tert-butyl-peroxy)-2,5-dimethylhexane, DBPMH), and the free volume holes in the samples were investigated by means of positron annihilation lifetime spectroscopy (PALS) measurement. The surface chemical structure, surface micromorphology and water diffusion of the samples after corona discharge treatment were studied by FTIR, SEM and EIS measurements, respectively. As the crosslinker weight ratio increased from 0.2 wt.% to 1.5 wt.%, the mean free volume hole size first decreased and then remained unchanged. However, the concentration of free volume holes did not vary as the crosslinker weight ratio increased. SEM morphologies show that surface cracks were produced on samples having high crosslinking levels after corona treatment. The water diffusion coefficient of samples after corona treatment increased from 3.13 × 10⁻¹⁰ cm² s⁻¹ to 17.68 × 10⁻¹⁰ cm² s⁻¹ in the initial immersion period, as the crosslinker weight ratio increased from 0.2 wt.% to 3.0 wt.%. The results indicated that deterioration of samples with high crosslinking levels were more serious and water repellency more easily lost. The corona resistance ability of low crosslinking level silicone rubber stems from internal low molecular weight molecules.

Enhancing the corona resistance of epoxy resin (EP) is crucial for ensuring the reliable operation of electrical equipment and power systems, and the incorporation of inorganic nanofillers into epoxy resin has shown significant potential in achieving this. In this study, functionalized graphene oxide (KHGO) was synthesized via a sol-gel method to enhance the corona resistance of EP with electrochemical impedance spectroscopy (EIS) used to assess the properties of KHGO/EP composites. Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS) verified the successful grafting of epoxy groups onto the GO surface. The thermal conductivity and stability of the KHGO/EP composite initially increased with KHGO content but declined when the content exceeded 1.2 wt.%. Positron annihilation lifetime spectroscopy (PALS) indicated that KHGO improved interfacial compatibility with EP compared to GO, with agglomeration occurring when KHGO content exceeded a threshold value (1.2 wt.%). EIS analysis revealed that the corona resistance of the KHGO/EP composite was optimal at a filler content of 0.9 wt.%. After corona treatment, the saturation water uptake of the 0.9 wt.% KHGO/EP composite decreased by 15% compared to pure EP with its porosity reduced to just 1/40th of that of pure EP. This study underscores that well-dispersed KHGO/EP composite exhibits excellent corona resistance property suggesting the potential for industrial applications in high-voltage equipment insulation.