The tremendous potential of zeolite membranes for efficient molecular separation via size-exclusion effects is highly desired by the energy and chemical industries, but its practical realization has been hindered by nonselective permeation through intercrystalline spaces and high resistance to intracrystalline diffusion in the conventional zeolite membranes of randomly oriented polycrystalline structures. Here, we report the synthesis of ZSM-5 zeolite nanosheets with very large aspect ratios and nanometer-scale thickness in the preferred straight channel direction. We used these ZSM-5 nanosheets to fabricate ultrathin (<500 nm) laminated membranes on macroporous alumina substrates by a simple dip-coating process and subsequent consolidation via vapor-phase crystallization. This ultrathin b-oriented ZSM-5 membrane has demonstrated extraordinary water flux combined with high salt rejection in pervaporation desalination for brines containing up to 24 weight % of dissolved NaCl. The ZSM-5 nanosheets may also offer opportunities to developing high-performance battery ion separators, catalysts, adsorbents, and thin-film sensors.

The separation of small molecule gases by membrane technologies can help performance enhancement and process intensification for emerging advanced fossil energy systems with CO₂ capture capacity. This paper reports the demonstration of controlled modification of zeolitic channel size for the MFI-type zeolite membranes to enhance the separation of small molecule gases such as O₂ and N₂. Pure-silica MFI-type zeolite membranes were synthesized on porous α-alumina disc substrates with and without an aluminum-containing thin skin on the outer surface of zeolite membrane. The membranes were subsequently modified by on-stream catalytic cracking deposition (CCD) of molecular silica to reduce the effective openings of the zeolitic channels. Such a pore modification caused the transition of gas permeation from the N₂-selective gaseous diffusion mechanism in the pristine membrane to the O₂-selective activated diffusion mechanism in the modified membrane. The experimental results indicated that the pore modification could be effectively limited within the aluminum-containing surface of the MFI zeolite membrane to minimize the mass transport resistance for O₂ permeation while maintaining its selectivity. The implications of pore modification on the size-exclusion-enabled gas selectivity were discussed based on the kinetic molecular theory. In light of the theoretical analysis, experimental investigation was performed to further enhance the membrane separation selectivity by chemical liquid deposition of silica into the undesirable intercrystalline spaces.