The controllable electrical and optical properties of two-dimensional tungsten disulfide (WS₂) attracted much attention in photocatalysis, but commercial development has been severely restricted by their restacking properties. Surfactant-assisted synthesis techniques can be considered as an effective option to break this bottleneck. In this work, the effect of surfactants including sodium dodecylbenzene sulfonate (SDBS), hexadecyltrimethylammonium bromide (CTAB), and polyvinylpyrrolidone (PVP) on the microstructure of WS₂/tourmaline composites prepared by coupled hydrothermal and calcination methods was explored. The WS₂ nanosheets were uniformly deposited on the tourmaline surface with the assistance of 1.0 mmol/L SDBS. Meanwhile, WS₂/Tour-SDBS exhibited the highest rhodamine B (RhB) degradation activity, which was 1.8 and 2.3 times higher than that of photocatalysts prepared with CTAB and PVP under the same conditions, respectively. This study provides a new tactic for the fabrication of high-performance WS₂-based composites.

Ni-based catalysts have been widely used in catalytic reactions by researchers due to their advantages such as abundant resources, high catalytic activity and lower prices than precious metals. However, the problems of easy agglomeration and poor dispersion of Ni-based catalysts have hindered their large-scale application. Therefore, it is necessary to select a suitable preparation method to reduce the agglomeration of the catalyst and improve its dispersion. In this paper, the Ni-NiAl₂O₄/tourmaline composite material was prepared by using the microwave hydrothermal reduction method. The most favorable conditions for preparing NiAl₂O₄/tourmaline are as follows: using TEOA as the additive, the microwave hydrothermal temperature is 220 °C, the calcination temperature is 800 °C, and the addition amount of tourmaline is 7.4 wt.%. NiAl₂O₄ has a good dispersion over the surface of tourmaline support and the optimal NiAl₂O₄/tourmaline catalyst exhibits a specific surface area of 106.5 m²/g. Metallic nickel was reduced at 650 °C to further obtain Ni-NiAl₂O₄/tourmaline composites. Finally, the Ni-NiAl₂O₄/tourmaline composites showed significantly improved catalytic dry reforming of methane (DRM) activity compared to Ni-NiAl₂O₄ sample under low-temperature conditions (500–600 °C), meaning that the tourmaline carrier could effectively optimize the low-temperature catalytic performance of Ni-NiAl₂O₄.