In the last few years, researchers have focused their attention on the synthesis of new catalyst structures based on or inspired by nature. Biotemplating involves the transfer of biological structures to inorganic materials through artificial mineralization processes. This approach offers the main advantage of allowing morphological control of the product, as a template with the desired morphology can be pre-determined, as long as it is found in nature. This way, natural evolution through millions of years can provide us with new synthetic pathways to develop some novel functional materials with advantageous properties, such as sophistication, miniaturization, hybridization, hierarchical organization, resistance, and adaptability to the required need. The field of application of these materials is very wide, covering nanomedicine, energy capture and storage, sensors, biocompatible materials, adsorbents, and catalysis. In the latter case, bio-inspired materials can be applied as catalysts requiring different types of active sites (i.e., redox, acidic, basic sites, or a combination of them) to a wide range of processes, including conventional thermal catalysis, photocatalysis, or electrocatalysis, among others. This review aims to cover current experimental studies in the field of biotemplating materials synthesis and their characterization, focusing on their application in heterogeneous catalysis.

The role of p-benzoquinone (BQ) as a photocatalyst in the synthesis of solketal under UV irradiation has been studied, along with the combined use of BQ/TiO₂ P25 as a photocatalytic system for the process. The presence of the O₂/O₂^−• redox couple is essential for the reaction to take place. However, experiments with p-benzoquinone as a superoxide radical scavenger failed, with the opposite effect of enhancing the reaction being observed. It was found that p-benzoquinone and oxygen compete for photogenerated electrons in the conduction band of titania. A redox equilibrium between p-benzoquinone and hydroquinone (H₂Q), mediated by the O₂/O₂^−• system, was identified as a key factor in enabling the reaction. Furthermore, EPR spin-trapping experiments confirmed the presence of the carbon-centered radical 2-hydroxypropan-2-yl, which was determined to be the main radical species involved in the process. Either acetone or 2-propanol can generate this radical, with the BQ/H₂Q redox system being pivotal in the formation of the hemiacetal intermediate. This intermediate is subsequently converted into the final acetal (solketal), with H₂Q acting as a photoacid through an excited-state proton transfer (ESPT) mechanism. The photoacid behavior of hydroquinone was confirmed using pyridine as a basic probe, as the formation of hydroquinone–pyridine adducts was detected by Raman spectroscopy.

Olive leaves (by-product from olive oil production in olive mills) were used as biotemplates to synthesize a titania-based artificial olive leaf (AOL). Scanning electron microscopy (SEM) images of AOL showed the successful replication of trichomes and internal structure channels present in olive leaves. The BET surface area of AOL was 52 m²·g⁻¹. X-ray diffraction (XRD) and Raman spectra revealed that the resulting solid was in the predominantly-anatase crystalline form (7.5 nm average particle size). Moreover, the synthesis led to a red-shift in light absorption as compared to reference anatase (gap energies of 2.98 and 3.2 eV, respectively). The presence of surface defects (as evidenced by X-ray photoelectron spectroscopy, XPS, and electron paramagnetic resonance spectroscopy, EPR) and doping elements (e.g., 1% nitrogen, observed by elemental analysis and XPS) could account for that. AOL was preliminarily tested as a catalyst for hydrogen production through glycerol photoreforming and exhibited an activity 64% higher than reference material Evonik P25 under solar irradiation and 144% greater under ultraviolet radiation (UV).

Pt-TiO₂ systems are the most widely used photocatalysts in the production of green hydrogen from glycerol photoreforming. To incorporate metals on the surface of materials, photodeposition is the most used method because it employs mild conditions. However, despite its use, there are some parameters that have not been deeply studied, such as the appropriate metal loading and the method itself, to obtain a better dispersion of Pt. In this work, six Pt-TiO₂ catalysts were synthesized by a classical photodeposition method employing UV radiation. The studied Pt wt.% range was 0.15–0.60 wt.%, being incorporated in one step or in subsequent ones. HRTEM analyses showed that both methods allowed a homogeneous distribution of Pt, and in both, the particle size was around 2.3–3.6 nm, increasing with metal loading. The photocatalytic activity of materials was tested in glycerol photoreforming under UV radiation, and the 0.45 wt.% Pt-containing solid that had been synthesized in one step was the one that allowed the highest hydrogen production. This might suggest that around 0.40% is the appropriate metal loading for hydrogen production under these conditions and that incorporating the desired metal percentage in one step is the most efficient method in terms of energy and time savings.

Solar glycerol photoreforming was investigated on Au-Ni/CeO₂ photocatalysts with an overall metal content equal to 1wt% and different Au/Ni weight ratios. The deposition of gold over ceria was performed by two different methods, deposition–precipitation and photoreduction. Deposition–precipitation was the best method to deposit gold on CeO₂ with the formation of small Au nanoparticles (around 4 nm). The most active sample (0.9 wt% Au-0.1 Ni wt%/CeO₂) provided a H₂ production rate of 350 µmol/gcat∙h, much higher than the corresponding monometallic samples. A higher amount of Ni led to detrimental effects in H₂ production, likely due to the covering of the gold surface active sites by Ni. On the contrary, the presence of a small amount of Ni (0.1 wt%) allowed a remarkable improvement of the Au/CeO₂ photocatalytic stability after consecutive runs of simulated solar irradiation. This finding, as well as the activation of synergistic effects, the improved charge carrier separation, and the exploitation of the localized surface plasmon resonance property of gold, led to the proposal of an alternative photocatalytic system to the most investigated TiO₂-based photocatalysts for H₂ production. The enhanced stability is promising to further foster the investigation of these photocatalysts applied to sustainable H₂ production.