Polysaccharide biomaterials have gained significant importance in the manufacture of nanoparticles used in colon-targeted drug delivery systems. These systems are a form of non-invasive oral therapy used in the treatment of various diseases. To achieve successful colonic delivery, the chemical, enzymatic and mucoadhesive barriers within the gastrointestinal (GI) tract must be analyzed. This will allow for the nanomaterials to cross these barriers and reach the colon. This review provides information on the development of nanoparticles made from various polysaccharides, which can overcome multiple barriers along the GI tract and affect encapsulation efficiency, drug protection, and release mechanisms upon arrival in the colon. Also, there is information disclosed about the size of the nanoparticles that are usually involved in the mechanisms of diffusion through the barriers in the GI tract, which may influence early drug degradation and release in the digestive tract.

In the present study water extractable arabinoxylans (WEAX) from a Mexican spring wheat flour (cv. Tacupeto F2001) were isolated, characterized and gelled and the gel rheological properties and microstructure were investigated. These WEAX presented an arabinose to xylose ratio of 0.66, a ferulic acid and diferulic acid content of 0.526 and 0.036 µg/mg WEAX, respectively and a Fourier Transform Infra-Red (FT-IR) spectrum typical of arabinoxylans. The intrinsic viscosity and viscosimetric molecular weight values for WEAX were 3.5 dL/g and 504 kDa, respectively. WEAX solution at 2% (w/v) formed gels induced by a laccase as cross-linking agent. Cured WEAX gels registered storage (G’) and loss (G’’) modulus values of 31 and 5 Pa, respectively and a diferulic acid content of 0.12 µg/mg WEAX, only traces of triferulic acid were detected. Scanning electron microscopy analysis of the lyophilized WEAX gels showed that this material resembles that of an imperfect honeycomb.

Due to their porous structure, aqueous environment and dietary fiber nature arabinoxylan (AX) gels could have potential applications for colon-specific therapeutic molecule delivery. In addition, prebiotic and health related effects of AX have been previously demonstrated. It has been also reported that cross-linked AX can be degraded by bacteria from the intestinal microbiota. However, AX gels have not been abundantly studied as carrier systems and there is no information available concerning their capability to entrap cells. In this regard, probiotic bacteria such as Bifidobacterium longum have been the focus of intense research activity lately. The objective of this research was to investigate the entrapment of probiotic B. longum in AX gels. AX solution at 2% (w/v) containing B. longum (1 × 10⁷ CFU/cm) formed gels induced by laccase as cross-linking agent. The entrapment of B. longum decreased gel elasticity from 31 to 23 Pa, probably by affecting the physical interactions taking place between WEAX chains. Images of AX gels containing B. longum viewed under a scanning electron microscope show the gel network with the bacterial cells entrapped inside. The microstructure of these gels resembles that of an imperfect honeycomb. The results suggest that AX gels can be potential candidates for the entrapment of probiotics.

Aggregation and coalescence are major drawbacks that contribute to polydispersity in microparticles and nanoparticles fabricated from diverse biopolymers. This study presents the evaluation of a novel method for the direct, electrospray-induced fabrication of small, CaCl₂/ethanol-hardened low methoxy pectin/arabinoxylans composite microbeads. The electrospray method was evaluated to control particle size by adjusting voltage, flux, and crosslinking solution content of CaCl₂/ethanol. A bead diameter of 1µm was set as reference to test the capability of this method. Insulin was chosen as a model carried molecule. Statistical analysis was a central composite rotatable design (CCRD) with a factorial arrangement of 2⁴. The variables studied were magnitude and particle size dispersion. For the determination of these variables, light diffraction techniques, scanning electron microscopy, transmission electron microscopy, and confocal laser scanning microscopy were used. Major interaction was found for ethanol and CaCl₂ as well as flow and voltage. Stable spherical structures of core–shell beads were obtained with neither aggregation nor coalescence for all treatments where ethanol was included in the crosslinking solution, and the average diameter within 1 ± 0.024 μm for 11 KV, 75% ethanol with 11% CaCl₂, and flow of 0.97 mL/h.