Solid-state electrolytes are widely expected to enhance the performance of lithium-ion batteries, providing higher energy density and improved safety. However, challenges still need to be solved in their practical application due to low ionic conductivity and high interfacial resistance at room temperature. In this study, we successfully developed a high-performance gel polymer electrolyte (GPEs) by blending poly(vinylidene fluoride-co-hexafluoropropylene)(PVDF-HFP) and polyacrylonitrile (PAN) through UV curing, cross-linking with ethoxylated trimethylolpropane triacrylate (ETPTA), and incorporating Li_6.4La₃Zr_1.4Ta_0.6O₁₂ (LLZTO). At room temperature, the ionic conductivity of the GPEs was 2.8 × 10⁻⁴ S/cm, with a lithium-ion transference number of 0.6. Moreover, during lithium plating/stripping tests, the assembled Li/PPEL/Li symmetric cell exhibited stable cycling for up to 600 h at a current density of 0.1 mA/cm². Notably, the GPEs enabled the LiFePO₄/GPEs/Li battery to achieve excellent performance, delivering high discharge capacities at room temperature (164.3 mAh g⁻¹ at 0.1 C and 88.8 mAh g⁻¹ at 1 C), with a capacity retention of 89.4% after 200 cycles at 0.5 C. Therefore, solid-state batteries using this electrolyte exhibit excellent performance, including adequate capacity and cycling stability.

Lithium-ion batteries have garnered significant attention owing to their exceptional energy density, extended lifespan, rapid charging capabilities, eco-friendly characteristics, and extensive application potential. These remarkable features establish them as a critical focus for advancing next-generation battery technologies. However, the commonly used organic liquid electrolytes in batteries are explosive, volatile, and possess specific toxic properties, resulting in persistent safety concerns that remain to be addressed. Composite polymer electrolytes (CPEs) exhibit enhanced safety and stable electrochemical performance, emerging as one of the most promising alternatives. However, single polymers often need to meet the multifaceted performance requirements of batteries. In this study, a composite polymer electrolyte was prepared using solution casting, consisting of a blend of polyurethane (TPU) and polyacrylonitrile (PAN), along with the ceramic filler Li_1.3Al_0.3Ti_1.7(PO₄)₃ (LATP) and lithium perchlorate (LiClO₄). The optimal formulation, which included 40 wt% TPU, 60 wt% PAN, and 10 wt% LATP, exhibited a commendable ionic conductivity of 2.1 × 10⁻⁴ S cm⁻¹, a lithium-ion transference number (t_Li⁺) of 0.60, and notable electrochemical stability at 30 °C. The LiFePO₄/Li battery assembled with this CPE demonstrated excellent cycling stability and rate capability at room temperature. It delivered a discharge specific capacity of 130 mAh g⁻¹ at 1C. Under a charge–discharge rate of 0.2C, the battery achieved a discharge specific capacity of 168 mAh g⁻¹, retaining 98% of its capacity after 100 cycles at 25 °C. Additionally, the CPE exhibited robust safety performance. Consequently, this composite polymer electrolyte holds significant promise for application in lithium-ion batteries.

Solid-state electrolytes are widely anticipated to revitalize high-energy-density and high-safety lithium-ion batteries. However, low ionic conductivity and high interfacial resistance at room temperature pose challenges for their practical application. In this work, the dual-matrix concept is applied to the design of a bilayer heterogeneous structure. The electrolyte in contact with the cathode blends PVDF-HFP and oxidation-resistant PAN. In contrast, the electrolyte in contact with the anode blends PVDF-HFP and reduction-resistant PEO. A UV-curing process was used to fabricate the bilayer heterostructure electrolyte. The heterostructure electrolyte exhibits an ionic conductivity of 4.27 × 10⁻⁴ S/cm and a Li⁺ transference number of 0.68 at room temperature. Additionally, when assembled into LiFePO₄/CPEs/Li batteries, it shows a high initial discharge capacity at room temperature (168 mAh g⁻¹ at 0.1 C and 60 mAh g⁻¹ at 2 C), with a capacity retention of 93.3% after 100 cycles at a current density of 0.2 C. Notably, at 60 °C, the battery maintains a discharge capacity of 90 mAh g⁻¹ at 2 C, with a capacity retention of 97.4% after 100 cycles at 0.2 C. Therefore, solid-state batteries using this bilayer heterogeneous structure electrolyte demonstrate promising performance, including effective capacity output and cycling stability.

Gel polymer electrolytes (GPEs) have high safety and excellent electrochemical performance, so applying GPEs in lithium batteries has received much attention. However, their poor lithium ion transfer number, cycling stability, and low room temperature ionic conductivity seriously affect the utilization of gel polymer electrolytes. This paper successfully synthesized flexible poly (vinylidene fluoride-hexafluoropropylene)–lithium titanium aluminum phosphate (PVDF-HFP-LATP) gel polymer electrolytes using the immersion precipitation method. The resulting GPE has a porous honeycomb structure, which ensures that the GPE has sufficient space to store the liquid electrolyte. The GPE has a high ionic conductivity of 1.03 ×10⁻³ S cm⁻¹ at room temperature (25 °C). The GPE was applied to LiFePO₄/GPE/Li batteries with good rate performance at room temperature. The discharge specific capacity of 1C was as high as 121.5 mAh/g, and the capacity retention rate was 94.0% after 300 cycles. These results indicate that PVDF-HFP-LATP-based GPEs have the advantage of simplifying the production process and can improve the utility of gel polymer lithium metal batteries.