This study presents the experimental results of fresh and hardened properties of concrete incorporating high-volume fly ash (HVFA). Two kinds of low-calcium fly ash with loss on ignition (LOI) of 5% and 8% were used as replacement for cement and/or fine aggregate of 0% (control), 20%, 40%, 50%, 60% and 80% by weight of the total cementitious materials. The properties of fresh concrete tested included the slump, air content, unit weight and setting time; those of hardened concrete determined included compressive strength, modulus of elasticity, flexural strength and drying shrinkage. Test results indicate that the concretes made with high-LOI (8%) fly ash can be successfully produced for structural concrete, which contains fly ash of up to 60% of the total cementitious materials. The high-LOI fly ash-concretes with higher replacement levels presented longer setting times. However, although both the fresh and hardened properties of high LOI fly ash concretes were inferior to those of the low-LOI (5%) fly ash concretes, the high modulus of elasticity, the adequate strength development characteristics both at early and later ages (up to 365 days) and the low dry shrinkage were observed when compared to those of the control concrete with a comparable 28-day compressive strength of 30 MPa.

This study focuses on evaluating the effects of the fineness of fly ash on the strength, fracture toughness, and fracture resistance of concrete. Three fineness levels of fly ash that respectively pass sieves—no. 175, no. 250, and no. 32—were used. In addition to the control concrete mixture without fly ash, two fly ash replacement levels of 10% and 20% by weight of the cementitious material were selected for the concrete mixture. The experimental results indicate that the compressive strength of the fly ash concrete decreases with the increase in the replacement ratio of fly ash but increases in conjunction with the fineness level of fly ash. The presence of finer fly ash can have beneficial effects on the fracture energy (G_F) of concrete at an early age (14 days) and attain a higher increment of G_F at a later age (56 days). The concrete containing finer fly ash was found to present larger critical stress intensity factors (K^S_IC) at various ages, and the K^S_IC also increases in conjunction with the fineness levels of fly ash.

This paper aims to experimentally investigate the effects of high volume cement replacement of blast furnace slag (BFS) on the bond, strength and durability of recycled aggregate concrete (RAC). Concrete mixtures were prepared containing 0%, 15%, 30%, 45%, 60% and 75% BFS with each of recycled aggregate and natural aggregate. Measurements of the compressive and bond strength, the resistance to chloride-ion penetration and the water permeability of concrete are reported. In addition, a microhardness test was also performed to evaluate the quality of interfacial transition zone (ITZ) in concrete. Test results of the bond strength and the compressive strength of RAC mixtures, in spite of the cement replacement amount with BFS, show that the concretes result in reduced strength when compared to natural aggregate concrete (NAC) mixtures, while the strength gains for the BFS-based concrete are higher than that of the reference mixtures without BFS at long-term ages. Incorporating BFS in concrete can inherently improve the durability properties by increasing higher resistance to chloride-ion penetration and lower water permeability. This improvement in the mechanical and durability properties of the BFS-based RAC mixture may be due to the additional pozzolanic reaction of BFS, which enhances the properties of ITZ in concrete, resulting in an improvement of the strength of concrete.

Expanded shale lightweight aggregates, as the coarse aggregates, were used to produce lightweight aggregate concrete (LWAC) in this research. At the fixed water-cement ratio, paste quantity, and aggregate volume, the effects of various aggregate gradations on the engineering properties of LWAC were investigated. Comparisons to normal-weight concrete (NWC) made under the same conditions were carried out. From the experimental results, using normal weight aggregates that follow the specification requirements (standard gradation) obtained similar NWC compressive strength to that using uniform-sized aggregates. However, the compressive strength of LWAC made using small uniform-sized aggregates was superior to that made from standard-grade aggregates. This is especially conspicuous under the low water-cement ratio. Even though the workability was affected, this problem could be overcome with developed chemical additive technology. The durability properties of concrete were approximately equal. Therefore, it is suggested that the aggregate gradation requirement of LWAC should be distinct from that of NWC. In high strength LWAC proportioning, following the standard gradation suggested by American Society for Testing and Materials (ASTM) is optional.

The effects of particle size of ground granulated blast furnace slag (GGBS) on the fracture energy, critical stress intensity, and strength of concrete are experimentally studied. Three fineness levels of GGBS of 4000, 5000, 6000 cm²/g were used. In addition to the control mixture without slag, two slag replacement levels of 20% and 40% by weight of the cementitious material were selected for preparing the concrete mixtures. The control mixture was designed to have a target compressive strength at 28 days of 62 MPa, while the water to cementitious material ratio was selected as 0.35 for all mixtures. Test results indicate that using finer slag in concrete may improve the filling effect and the reactivity of slag, resulting in a larger strength enhancement. The compressive strength of slag concrete was found to increase in conjunction with the fineness level of the slag presented in the mixture. Use of finer slag presents a beneficial effect on the fracture energy (G_F) of concrete, even at an early age, and attains a higher increment of G_F at later age (56 days). This implicates that the finer slag can have a unique effect on the enhancement of the fracture resistance of concrete. The test results of the critical stress intensity factor (K^S_IC) of the slag concretes have a similar tendency as that of the fracture energy, indicating that the finer slag may present an increase in the fracture toughness of concrete.