Gas nitriding, as a surface modification technology to improve the wear resistance of workpiece surfaces, is widely used in wind turbine gears, pressure vessel gears, high-precision die casting abrasives, and other areas. However, the gas nitriding time is too long, reaching 40–60 h, which reduces the efficiency of nitriding and hinders the development of gas nitriding. Therefore, various accelerating methods are born accordingly. This review first introduces the basic principle, microstructure, and process parameters of conventional gas nitriding. Then, five common accelerating methods are summarized: process parameter optimization, surface mechanical nano-crystallization, surface-active catalysis, surface pre-oxidation, and surface laser treatment. Then, the effect of acceleration methods on gas nitriding is analyzed for the acceleration mechanism, nitriding behavior, and nitriding efficiency. Finally, the technical economy of the acceleration methods is compared for three aspects: energy consumption, carbon dioxide emission, and cost. And, the technical maturity of the acceleration methods is compared according to technology readiness level (TRL) technology. Based on the above content, the advantages and disadvantages of the five accelerating methods are reviewed, and the concept of a multi-technology collaborative processing acceleration method is proposed.

The wide application of magnesium alloys as biodegradable implant materials is limited because of their fast degradation rate. Hydroxyapatite (HA) coating can reduce the degradation rate of Mg alloys and improve the biological activity of Mg alloys, and has the ability of bone induction and bone conduction. The preparation of HA coating on the surface of degradable Mg alloys can improve the existing problems, to a certain extent. This paper reviewed different preparation methods of HA coatings on biodegradable Mg alloys, and their effects on magnesium alloys’ degradation, biocompatibility, and osteogenic properties. However, no coating prepared can meet the above requirements. There was a lack of systematic research on the degradation of coating samples in vivo, and the osteogenic performance. Therefore, future research can focus on combining existing coating preparation technology and complementary advantages to develop new coating preparation techniques, to obtain more balanced coatings. Second, further study on the metabolic mechanism of HA-coated Mg alloys in vivo can help to predict its degradation behavior, and finally achieve controllable degradation, and further promote the study of the osteogenic effect of HA-coated Mg alloys in vivo.

In recent years, biodegradable magnesium (Mg) alloys have attracted the attention of many researchers due to their mechanical properties, excellent biocompatibility and unique biodegradability. Many Mg alloy implants have been successfully applied in clinical medicine, and they are considered to be promising biological materials. In this article, we review the latest research progress in biodegradable Mg alloys, including research on high-performance Mg alloys, bioactive coatings and actual or potential clinical applications of Mg alloys. Finally, we review the research and development direction of biodegradable Mg alloys. This article has a guiding significance for future development and application of high-performance biodegradable Mg alloys, promoting the future advancement of the magnesium alloy research field, especially in biomedicine.

An hypereutectic Al–18Si alloy was modified via an Al–3B master alloy. The effect of the added Al–3B and the modification temperature on the microstructure, tensile fracture morphologies, and mechanical properties of the alloy were investigated using an optical microscope, Image–Pro Plus 6.0, a scanning electron microscope, and a universal testing machine. The results show that the size of the primary Si and its fraction decreased at first, and then increased as an additional amount of Al–3B was added. When the added Al–3B reached 0.2 wt %, the fraction of the primary Si in the Al–18Si alloy decreased with an increase in temperature. Compared with the unmodified Al–18Si alloy, the tensile strength and elongation of the alloy modified at 850 °C with 0.2 wt % Al–3B increased by 25% and 81%, respectively. The tensile fracture of the modified Al–18Si alloy exhibited partial ductile fracture characteristics, but there were more areas with ductile characteristics compared with that of the unmodified Al–18Si alloy.