Cementation is the baseline technology for conditioning of low to intermediate level radioactive waste. Geopolymers, a class of alkali activated binders, are a promising new material for radioactive waste treatment. Coal fly-ash based geopolymers are a low-cost, low greenhouse gas footprint alternative to metakaolin based materials. Both the grouting of sludge/powders/liquids and encapsulation of solids/compacted waste rely on the grout maintaining optimal flow (rheological properties) during the mixing and pouring operations, and achieving a set leading to proper long term solidification (mechanical properties). The initial and final setting time for fly-ash geopolymer paste, based on the SRPS EN 196-3 standard, has been measured upon irradiation by gamma rays in a 60Co reference field positioned with a kerma air rate of 3.42 mGys–1. The binder paste was prepared using fly-ash from the TENT B power plant's electrostatic filters without further sieving, activated by water glass with module 1.5 and mixed with distilled water until a satisfactory flow was obtained, and poured into the sample and control molds. The initial and final setting times for the irradiated sample and non-irradiated control were determined by the Vicat apparatus. The irradiated sample demonstrated an 11 % shorter initial setting time, and 16 % shorter final setting time, compared to the control.

An investigation of the effect of gamma radiation was carried out on the setting time of alkali-activated binder paste. Mechanically activated coal fly ash (FA), ground granulated blast furnace slag (BFS), and their 1:1 mass mixture (MIX) were activated by water glass with a module of 1.5. Fresh paste was cast into molds and exposed to Co-60 gamma radiation, at a dose rate of 9.62–9.53 Gy/h, until the final setting. The initial and final setting times were determined by measuring the penetration of the Vicat needle at regular intervals. The initial setting times were 1 h 3 min for BFS, 1 h 55 min for MIX, and 3 h 28 min for FA. The final setting times were 1 h 10 min for BFS, 2 h 13 min for MIX, and 4 h 1 min for FA. The received doses were 8.02 Gy for BFS, 17.54 Gy for MIX, and 34.14 Gy for FA. Exposure to gamma radiation resulted in a shorter initial setting time for BFS, a shorter final setting time for FA, and results with an insufficiently visible impact on MIX. For dose rates in the 9–10 Gy/h range, the irradiation by Co-60 gamma rays during setting did not lead to flash, nor did it delay the setting of alkali-activated binder pastes.