This paper reports on an investigation treating a hard-milled surface as a surface undergoing severe plastic deformation at elevated temperatures. This surface exhibits remarkable magnetic anisotropy (expressed in term of Barkhausen noise). This paper also shows that Barkhausen noise emission in a hard-milled surface is a function of tool wear and the corresponding microstructure transformations initiated in the tool/machined surface interface. The paper discusses the specific character of Barkhausen noise bursts and the unusually high magnitude of Barkhausen noise pulses, especially at a low degree of tool wear. The main causes can be seen in specific structures and the corresponding domain configurations formed during rapid cooling following surface heating. Domains are not randomly but preferentially oriented in the direction of the cutting speed. Barkhausen noise signals (measured in two perpendicular directions such as cutting speed and feed direction) indicate that the mechanism of Bloch wall motion during cyclic magnetization in hard-milled surfaces differs from surfaces produced by grinding cycles or the raw surface after heat treatment.

This study is focused on the asymmetrical Barkhausen noise emission of a hard milled surface during cyclic magnetisation. The Barkhausen noise is studied as a function of the magnetising voltage and the hard milled surface is compared with a surface after heat treatment. The asymmetry in the Barkhausen noise emission after hard milling occurs due to the typical “sandwich” structure and the different magnetic hardnesses of the different layers beneath the free surface. Furthermore, this asymmetry is also due to the preferential orientation of the matrix in the direction of the cutting speed and magnetostatic fields, which hinder or favour the premagnetising process.

This paper deals with analysis of surface integrity of steel after electro discharge machining (EDM), water jet machining, (WJM) laser beam machining (LBM) and plasma beam machining (PBM). The paper discusses surface integrity expressed in sur...

This study is focused on analysing residual stresses (RSs) after turning high-tempered bearing steel through the use of the X-ray diffraction (XRD) technique. Phase transformations expressed in terms of the near-surface white layer (WL) and the corresponding microhardness profiles are correlated with the RSs as well as the depth of the RS profiles. Normal and shear components of RS and FWHM (full width at half maximum) of the diffraction peaks are analysed as a function of cutting insert flank wear as well as the cutting speed. It was found that the influence of tool wear prevails over cutting speed, RSs tend to shift into the compressive region with increasing tool flank wear, and the valuable shear components of RSs can be found in the near-surface region when the cutting inserts of lower flank wear are employed. The increasing flank wear also increases the depth in which the compressive RSs can be found. Furthermore, surface RSs are affected by the phase transformation process (formation of re-hardened WL) as well as the superimposing mechanical and thermal load.

This paper investigates surface state after turning of the high tempered bearing steel 100Cr6 with a hardness of 40 HRC. White layer (WL) thickness and its microhardness, as well as surface roughness, are investigated as a function of tool flank wear VB as well as cutting speed v_c. The mechanical and thermal load of the machined surface were analysed in order to provide a deeper insight into their superimposing contribution. Cutting energy expressed in terms of cutting force was analyses as that consumed for chip formation F_γ and consumed in the flank wear land F_α. It was found that the mechanical energy expressed in terms of the shear components of the F_α grows with VB, converts to the heat and strongly affects the thickness of the re-hardened layer. Furthermore, the superimposing contribution of the heat generation and its duration in the VB region should also be taken into account. It was also found that the influence of VB predominates over the variable cutting speed.