Self-assembled nanolayering structures have been reported in resin-dentin interfaces created by adhesives that contain 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP). These structures have been hypothesized to contribute to bond durability. The objective of the present study was to determine the extent of nanolayering in resin-dentin interfaces after application of commercialized 10-MDP-containing self-etch and universal adhesives to human dentin. Seven commercialized adhesives were examined: Adhese Universal (Ivoclar-Vivadent), All-Bond Universal (Bisco, Inc.), Clearfil SE Bond 2, Clearfil S3 Bond Plus, Clearfil Universal Bond (all from Kuraray Noritake Dental Inc.), G-Premio Bond (GC Corp.), and Scotchbond Universal (3M ESPE). Each adhesive was applied in the self-etch mode on midcoronal dentin according to the respective manufacturer’s instructions. Bonded specimens (n = 6) were covered with flowable resin composite, processed for transmission electron microscopy, and examined at 30 random sites without staining. Thin-film glancing angle X-ray diffraction (XRD) was used to detect the characteristic peaks exhibited by nanolayering (n = 4). The control consisted of 15%wt, 10%wt, and 5%wt 10-MDP (DM Healthcare Products, Inc.) dissolved in a mixed solvent (ethanol and water weight ratio 9:8, with photoinitiators). Experimental primers were applied to dentin for 20 s, covered with hydrophobic resin layer, and examined in the same manner. Profuse nanolayering with highly ordered periodicity (~3.7 nm wide) was observed adjacent to partially dissolved apatite crystallites in dentin treated with the 15% 10-MDP primer. Three peaks in the 2θ range of 2.40° (3.68 nm), 4.78° (1.85 nm), and 7.18° (1.23 nm) were identified from thin-film XRD. Reduction in the extent of nanolayering was observed in the 10% and 5% 10-MDP experimental primer-dentin interface along with lower intensity XRD peaks. Nanolayering and characteristic XRD peaks were rarely observed in specimens prepared from the commercialized adhesives. The sparsity of nanolayering in resin-dentin interfaces created by commercialized adhesives challenges its clinical effectiveness as a mechanism for improving bond longevity in dentin bonding.

Instability of resin-dentin bonds is the Achilles’ heel of adhesive dentistry. To address this problem, a chelate-and-rinse extrafibrillar dentin demineralization strategy has been developed that keeps intrafibrillar minerals within collagen fibrils intact to prevent activation of endogenous proteases that are responsible for collagen degradation within hybrid layers. The objective of the present study was to evaluate the potential of using chitosan >40 kDa as an antimicrobial extrafibrillar dentin-chelating agent to enhance bond durability. Transmission electron microscopy provided evidence for retention of intrafibrillar minerals and smear plugs in dentin conditioned with 1 wt% chitosan. Analyzed by Kruskal-Wallis analysis of variance, Dunn’s statistic, and separate Mann-Whitney tests, tensile bond strengths to wet- and dry-bonded dentin indicated that chelating dentin with chitosan for 60 s prior to bonding did not result in a significant decline in resin-dentin bond strength when compared with that of phosphoric acid etching (P > 0.05). Gelatinolytic activity within the hybrid layers was examined via in situ zymography after 24-h storage or after thermomechanical cycling and analyzed with 3-factor analysis of variance. After 24 h, enzymatic activity was detected only within completely demineralized phosphoric acid–etched dentin, with values derived from dry bonding significantly higher than those derived from wet bonding (P < 0.05). Negligible fluorescence was detected within hybrid layers when dentin was conditioned with chitosan, even after thermomechanical cycling, as compared with the controls. Reduction in water permeability in chitosan-conditioned dentin, attributed to smear plug retention, also fostered long-term bond stability. Antibacterial testing performed with live/dead staining indicated that the acetic acid–solubilized chitosan possessed antibacterial activities against 3 single-species biofilms: Streptococcus mutans, Actinomyces naeslundii, and Enterococcus faecalis. Taken together, the new chitosan-based extrafibrillar demineralization strategy retains intrafibrillar minerals, reduces endogenous protease-initiated collagen degradation, prevents water permeation within hybrid layers, and kills bacteria on dentin surfaces, which are crucial factors for enhancing resin-dentin bond durability.

There is limited literature on the polishability of new launched nanofilled and nanohybrid. The aim of this study is to evaluate the polishability of nanofilled and nanohybrid composites by measuring surface roughness and gloss values and explore the surface qualities of composite before and after polishing in vitro. One nanofilled resin composite, two nanohybrid resin composites and one microhybrid resin composite were selected. All specimens were light cured against celluloid matrix strips. Then surface roughness(Ra) and gloss(GU) values were tested as negative control. Specimens were roughened with a 600-grit silicon carbide paper for 30 s to serve as positive control and then polished with Sof-Lex polishing disk system. Mean Ra and GU values of each step were measured with a profilometer and a small-area glossmeter. The surface qualities were observed by scanning electron microscope. Ra values of polished surfaces were significantly higher than negative control and lower than positive control(P < 0.05). All materials showed no significant difference on Ra values after polishing(P > 0.05). GU values of polished surfaces were significantly lower than negative control and higher than positive control(P < 0.05). After polishing the microhybrid resin composite showed lower GU values than nanofilled and nanohybrid resin composite groups. The SEM images showed surface textures and irregularities were corresponded to the results of surface roughness and gloss. No significant differences were noted on surface roughness among nanofilled, nanohybrid, and microhybrid composites after polishing with Sof-Lex disc system. Microhybrid composite presented lower gloss values than nanofilled and nanohybrid resin composites.