SUMMARY: Objective: The objective of this study was to evaluate the influence of adhesives with different 10-MDP concentrations on the shear bond strength of a resin cement to zirconia. Methods and Materials: Six experimental adhesives were prepared with the following composition: camphorquinone, 1,2-diaminobenzene, butylhydroxytoluene, diphenyliodonium hexafluorophosphate, 2-hydroxyethyl methacrylate triethylene glycol dimethacrylate, ethoxylated bisphenol A glycol dimethacrylate, urethane dimethacrylate, bisphenol A diglycidyl methacrylate, and ethanol. The 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) monomer was added at 0wt%, 3wt%, 6wt%, 9wt%, 12wt%, or 15wt%. Three commercially available adhesives were evaluated: Single Bond Universal, Single Bond 2, and Signum Zirconia Bond. Resin cement cylinders made with RelyX Ultimate were bonded to yttria-stabilized tetragonal zirconia polycrystal with one of the evaluated adhesives and were subjected to the shear bond strength evaluation. Failure modes were analyzed with a stereoscopic loupe. Statistical analyses were performed with one-way analysis of variance and the Tukey's Honestly Significant Difference test (α=0.05). Pearson's was used to correlate the percentage of 10-MDP in the experimental adhesives and shear bond strength. Results: There were significant differences between adhesives (p<0.00001). The highest shear bond strength values were obtained with the Signum Zirconia Bond and Single Bond Universal. Single Bond 2 showed the lowest values. There were no differences between experimental adhesives. All groups showed adhesives failures. A nonlinear correlation was found between bond strength and percentage of 10-MDP in experimental adhesives (r=0.872). Conclusions: The commercially available adhesives indicated for bonding to zirconia showed the highest bonding values.

Development of new materials for tooth bleaching justifies the need for studies to evaluate the changes in the enamel surface caused by different bleaching protocols. The aim of this study was to evaluate the bovine dental enamel wear in function of different bleaching gel protocols, acid etching and pH variation. Sixty fragments of bovine teeth were cut, obtaining a control and test areas. In the test area, one half received etching followed by a bleaching gel application, and the other half, only the bleaching gel. The fragments were randomly divided into six groups (n=10), each one received one bleaching session with five hydrogen peroxide gel applications of 8 min, activated with hybrid light, diode laser/blue LED (HL) or diode laser/violet LED (VHL) (experimental): Control (C); 35% Total Blanc Office (TBO35HL); 35% Lase Peroxide Sensy (LPS35HL); 25% Lase Peroxide Sensy II (LPS25HL); 15% Lase Peroxide Lite (LPL15HL); and 10% hydrogen peroxide (experimental) (EXP10VHL). pH values were determined by a pHmeter at the initial and final time periods. Specimens were stored, subjected to simulated brushing cycles, and the superficial wear was determined (μm). ANOVA and Tukey´s tests were applied (α=0.05). The pH showed a slight decrease, except for Group LPL15HL. Group LPS25HL showed the highest degree of wear, with and without etching. There was a decrease from the initial to the final pH. Different bleaching gels were able to increase the surface wear values after simulated brushing. Acid etching before bleaching increased surface wear values in all groups.

The use of light sources in the bleaching process reduces the time required and promotes satisfactory results. However, these light sources can cause an increase in the pulp temperature. Objective The purpose of the present study was to measure the increase in intrapulpal temperature induced by different light-activated bleaching procedures with and without the use of a bleaching gel. Material and Methods A human maxillary central incisor was sectioned 2 mm below the cementoenamel junction. A K-type thermocouple probe was introduced into the pulp chamber. A 35% hydrogen peroxide bleaching gel was applied to the vestibular tooth surface. The light units used were a conventional halogen, a hybrid light (only LED and LED/Laser), a high intensity LED, and a green LED light. Temperature increase values were compared by two-way ANOVA and Tukey´s tests (p<0.05). Results There were statistically significant differences in temperature increases between the different light sources used and between the same light sources with and without the use of a bleaching gel. The presence of a bleaching gel generated an increase in intra-pulpal temperature in groups activated with halogen light, hybrid light, and high intensity LED. Compared to the other light sources, the conventional halogen lamp applied over the bleaching gel induced a significant increase in temperature (3.83±0.41°C). The green LED unit with and without gel application did not produce any significant intrapulpal temperature variations. Conclusion In the present study, the conventional halogen lamp caused the highest increase in intrapulpal temperature, and the green LED caused the least. There was an increase in temperature with all lights tested and the maximum temperature remained below the critical level (5.5°C). The addition of a bleaching gel led to a higher increase in intrapulpal temperatures.

The aim of the present in vitro study was to evaluate the temperature variation inside the pulp chamber during light-activation of the adhesive and resin composite layers with different light sources. Cavities measuring 8x10 mm were prepared on the buccal surface of bovine incisors, leaving a remaining dentin thickness of 1 mm. Specimens were placed in a 37±1 °C water bath to standardize the temperature. The temperature in the pulp chamber was measured every 10 s during 40 s of light activation of the adhesive system (SBMP-3M/ESPE) and in the three consecutive 1-mm-thick layers of resin composite (Z250-3M/ESPE). Three light source devices were evaluated: Elipar 2500 (QTH), LD Max (LED low irradiance) and VALO (LED high irradiance). The results were submitted to one-way ANOVA with repeated measures and Tukey's test, both with p<0.001. The exothermic reaction warming was observed in the Z250 increments, but not in the SBMP. The high irradiance LED showed a higher temperature average (42.7±1.56 °C), followed by the quartz-tungsten-halogen light (40.6±0.67 °C) and the lower irradiance LED (37.8±0.12 °C). Higher temperature increases were observed with the adhesive and the first resin composite increment light-activation, regardless of the employed light source. From the second increment of Z250, the restorative material acted as a dispersive structure of heat, reducing temperature increases. Regardless the light source and restorative step, the temperature increased with the irradiation time. It may be concluded that the light source, irradiation time and resin composite thickness interfered in the temperature variation inside the pulp chamber.