Objective: The objective of this study is to present a case report in which the injectable composite resin technique was used as a restorative alternative for dental re-anatomization in a patient with cleft lip and palate and aesthetic complaints. Materials and Methods: The treatment plan included the re-anatomization of the maxillary premolars and canines using a flowable composite resin. This resin was injected and cured through a transparent matrix, which was a copy of the diagnostic wax-up model. Some parameters such as application time and marginal adaptation were also observed when performing the restorations. Additionally, old composite resin restorations on the upper lateral incisors were replaced using the incremental technique with conventional resins, which helped to assess color stability and fracture/wear deterioration for both restorative techniques. Results: The clinical case report shows that the injectable technique was a simple and quick method for restoring the anatomy of teeth (shape and contour) in one session, since the injectable resin can be easily applied in interproximal areas without the need to manually sculpt the resin. In this case, no clinical, visual, or photographic differences were found in marginal discoloration, color stability, and fracture/wear deterioration for the two restorative techniques after one year of follow-up. Conclusions: The professional may have another clinical option for restorative treatment in the case of small re-anatomizations. In addition, the injectable technique seems to require less operator skill and chair time and better marginal adaptation in cases of small anatomical changes.

The present in vitro study incorporated niobium oxyhydroxide fillers into an experimental high-viscosity bulk-fill resin composite to improve its mechanical performance and provide it a bioactive potential.

This study investigated the combined effects of adding niobium–fluoride (NbF₅) nanoparticles to a pit-and-fissure sealant. One resin sealant was reinforced with varying amounts of nanoparticles (0.3, 0.6, and 0.9 wt%). The surface hardness (SH), energy-dispersive X-ray spectroscopy (EDX), surface roughness (Ra), color change (ΔE), and mineral deposition were assessed. Bovine enamel blocks were subjected to demineralization and pH-cycling for SH. The elemental composition and Ca/P ratio were evaluated using EDX, while the mineral deposition was measured using Fourier transform infrared spectroscopy (FTIR). Data were analyzed using ANOVA and Tukey’s test for the SH and EDX, ΔE, and Kruskal–Wallis for the Ra. The NbF₅ modification increased the SH, with the 0.9 wt% sealant exhibiting higher SH values, and the 0.3 wt% one exhibiting significant differences compared to the control and the 0.9 wt% (p = 0.00) samples, even after pH-cycling. For the EDX analysis, the 0.3 and 0.6 wt% samples exhibited higher Ca/P ratios, with the 0.3% one showing evidence of P-O crystal formation. There was no significant difference in the Ra (p = 0.458), and the 0.6 and 0.9 wt% ones showed lower ΔE values compared to the control. The 0.3 wt% NbF₅ demonstrated improved overall properties, making these results particularly promising for preventing tooth decay, reducing demineralization through increased ions release and promoting remineralization in posterior teeth.