The Congo Red dye was removed from a simulated textile wastewater solution using fly ash from a local power plant. The characterisation of fly ash was studied in detail by SEM, EDX, XRD, FTIR, BET surface area and TGA techniques. The influence of four parameters (contact time, initial concentration, adsorbent dose, and temperature) was analysed, the results showing that the adsorption capacity depends on these parameters. Thermodynamic and regeneration investigations as well are presented. The fit to pseudo-second-order kinetics models suggests that the removal process is a chemical adsorption. The Langmuir model fitted the experimental data, with a maximum adsorption capacity of 22.12 mg/g. The research is a preliminary case study that highlights that fly ash posed a very good potential as a material for Congo Red dye removal.

Sustained research and development work on the utilization of waste (fly ash and silica fume) for various productive uses have been carried out. In the construction industry, major attention has been devoted to the use of fly ash and silica fume in concrete as addition to or as cement replacement. The utilization of a solid waste, fly ash and silica fume, in polymer concrete was reported in this paper including the effects on the compressive strength, flexural strength, and split tensile strength. The results show the influence of fly ash and silica fume content on the mechanical properties of polymer concrete with epoxy resin. The fillers improved the mechanical characteristics of polymer concrete compared to that of polymer concrete without filler: the compressive strength of polymer concrete with fly ash content was favorably influenced by the filler compound to polymer concrete with silica fume.

This work highlights new insights into the performance of TiO₂ doped with noble metal catalysts for the photocatalytic degradation of organic water pollutants. Different samples of titanium dioxide doped with noble metals (Au and Pd) were successfully synthesized via incipient wet impregnation (IWI) and ultrasound-assisted impregnation (US) methods. X-ray diffraction, scanning electron microscopy and UV-Vis reflectance spectroscopy were used for the characterization of the obtained materials. Their photocatalytic efficiency was investigated in aqueous suspension thorough a series of laboratory tests performed under ultraviolet (UV-A) irradiation conditions using 2,4 dinitrophenol (2,4 DNP) as a target molecule. The results clearly show that the method used for the catalyst synthesis affects its photocatalytic activity. It was found that the samples prepared by the IWI method exhibited high photocatalytic activity, and the removal rate obtained with TiO₂-Pd/IWI was higher than that found for TiO₂-Au/IWI. Furthermore, for the best catalyst, some extra photocatalytic experiments were conducted with rhodamine 6G (R6G), a highly stable molecule with a very different chemical structure to 2,4 DNP, in order to check the reactivity of this material. Moreover, the recycling experiments carried out with TiO₂-Pd/IWI clearly demonstrated the high photocatalytic stability of this material for the degradation of 2,4 DNP. All of the collected data confirmed the interesting photocatalytic potential of the selected catalyst in the elimination of organic pollutants with no obvious change in its reactivity after four reaction cycles, which is very promising for promoting future applications in water depollution.