This work highlights new insights into the performance of TiO₂ doped with noble metal catalysts for the photocatalytic degradation of organic water pollutants. Different samples of titanium dioxide doped with noble metals (Au and Pd) were successfully synthesized via incipient wet impregnation (IWI) and ultrasound-assisted impregnation (US) methods. X-ray diffraction, scanning electron microscopy and UV-Vis reflectance spectroscopy were used for the characterization of the obtained materials. Their photocatalytic efficiency was investigated in aqueous suspension thorough a series of laboratory tests performed under ultraviolet (UV-A) irradiation conditions using 2,4 dinitrophenol (2,4 DNP) as a target molecule. The results clearly show that the method used for the catalyst synthesis affects its photocatalytic activity. It was found that the samples prepared by the IWI method exhibited high photocatalytic activity, and the removal rate obtained with TiO₂-Pd/IWI was higher than that found for TiO₂-Au/IWI. Furthermore, for the best catalyst, some extra photocatalytic experiments were conducted with rhodamine 6G (R6G), a highly stable molecule with a very different chemical structure to 2,4 DNP, in order to check the reactivity of this material. Moreover, the recycling experiments carried out with TiO₂-Pd/IWI clearly demonstrated the high photocatalytic stability of this material for the degradation of 2,4 DNP. All of the collected data confirmed the interesting photocatalytic potential of the selected catalyst in the elimination of organic pollutants with no obvious change in its reactivity after four reaction cycles, which is very promising for promoting future applications in water depollution.

Over the last decade, researchers have been concerned with improving metallic biomaterials with proper and suitable properties for the human body. Ti-based alloys are widely used in the medical field for their good mechanical properties, corrosion resistance and biocompatibility. The TiMoZrTa system (TMZT) evidenced adequate mechanical properties, was closer to the human bone, and had a good biocompatibility. In order to highlight the osseointegration of the implants, a layer of hydroxyapatite (HA) was deposited using a biomimetic method, which simulates the natural growth of the bone. The coatings were examined by scanning electron microscopy (SEM), X-ray diffraction (XRD), micro indentation tests and contact angle. The data obtained show that the layer deposited on TiMoZrTa (TMZT) support is hydroxyapatite. Modifying the surface of titanium alloys represents a viable solution for increasing the osseointegration of materials used as implants. The studied coatings demonstrate a positive potential for use as dental and orthopedic implants.

In the present study the adsorption of Reactive Blue 19 dye on the hydroxyapatite (HAp) nanopowders was investigated. The batch adsorption experiments were performed by monitoring the adsorbent dosage, contact time, dye solution concentration, pH and temperature. At pH 3 and 20°C, high dye removal rates of about 95.58% and 86.95% for the uncalcined and calcined nanohydroxyapatites, respectively, were obtained. The kinetic studies indicated the dye adsorption onto nanohydroxyapatite samples to follow a pseudo-second order model. The Langmuir isotherm was found to be the best to represent the equilibrium with experimental data. The maximum adsorption capacity of uncalcined and calcined nanohydroxyapatite samples has been found to be 90.09 mg/g and 74.97 mg/g, respectively.