The development of high-efficiency multi-wire submerged arc welding technology in bridge engineering has been limited due to the high mechanical performance standards required. In this paper, weld metal was obtained by welding at three different high heat inputs with the laboratory-developed high-efficiency submerged arc welding wire for bridges. The effect of changing different high heat inputs on the microstructure and impact toughness of high efficiency submerged arc weld metal was systematically investigated by cutting and Charpy V-notch impact tests at −40 °C, using optical microscopy, scanning electron microscopy, energy-dispersive electron spectroscopy, electron backscatter diffraction, and transmission electron microscopy to characterize and analyze. With the increase in heat input from 50 kJ/cm to 100 kJ/cm, the impact absorption energy decreased significantly from 130 J to 38 J. The number of inclusions in the weld metal significantly decreased and the size increased, which led to a significant decrease in the number of inclusions that effectively promote acicular ferrite nucleation, further leading to a decrease in the proportion of acicular ferrite in the weld metal. At the same time, the microstructure of the weld metal was significantly coarsened, the percentage of high-angle grain boundaries was decreased, and the size of martensite/austenite constituents was significantly increased monotonically. The crack initiation energy was reduced by the coarsened martensite/austenite constituents and inclusions, which produced larger local stress concentrations, and the crack propagation was easier due to the coarsened microstructure and lower critical stress for crack instability propagation. The martensite/austenite constituents and inclusions in large sizes worked together to cause premature cleavage fracture of the impact specimen, which significantly deteriorated the impact toughness. The heat input should not exceed 75 kJ/cm for high-efficiency submerged arc welding wires for bridges.

The mechanical properties of a coarse-grained heat-affected zone (CGHAZ) are affected by welding thermal cycling with varied heat input (E_j), but its effect on tensile properties is rarely studied. In the present work, E_j = 15, 35, 55, 75 kJ/cm CGHAZ samples were prepared via Gleeble^TM (St. Paul, MN, USA) for a novel V-Ti-N microalloyed weathering steel. The tensile properties of CGHAZ with varied E_j were evaluated. The results indicated that mixed microstructures dominated by lath bainitic ferrite (LBF) and granular bainitic ferrite (GBF) were obtained at E_j = 15 and 35 kJ/cm, respectively, while a mixed microstructure composed of GBF, intragranular acicular ferrite (IGAF), and polygon ferrite (PF) formed at E_j = 55 and 75 kJ/cm, apart from martensite/austenite (M/A) constituents in each E_j condition. The above variation tendency in the microstructure with the increase in E_j led to coarsening of low-angle grain boundaries (LAGBs) and a decrease in dislocation density, which in turn resulted in a yield strength (YS) decrease from 480 MPa to 416 MPa. The mean equivalent diameter (MED), defined by the misorientation tolerance angles (MTAs) ranging from 2–6°, had the strongest contribution to YS due to their higher fitting coefficient of the Hall–Petch relationship. In addition, the increase in the average size (d_M/A) of M/A constituents from 0.98 μm to 1.81 μm and in their area fraction (f_M/A) from 3.11% to 4.42% enhanced the strain-hardening stress. The yield strength ratio (YR) reduced as the E_j increased, and the lower density and more uniform dislocations inside the ferrite led to a uniform elongation (uE) increase from 9.5% to 18.6%.

In this paper, the influence of the silicon (Si) content on microstructure and impact property of submerged arc weld metals (WMs) for weathering bridge steel was clarified. Actual submerged arc welding (SAW) was carried out to produce WMs with 0.18 wt.%, 0.36 wt.%, 0.51 wt.%, and 0.60 wt.% of Si. The low temperature impact property of weld metal was detected, and the weld microstructures were characterized by optical microscopy (OM), scanning and transmission electron microscope (SEM and TEM), and electron backscatter diffraction (EBSD). The results indicate that WMs consist of polygon ferrite (PF), acicular ferrite (AF), granular bainitic ferrite (GBF), and martensite/austenite (M/A) constituents in each Si content. With increasing Si, the proportion of PF increased, while AF and GBF coarsened, the area fraction, f_M/A, and the mean size, d_M/A, of M/A constituents increased, the number of inclusions decreased, but the size increased. Further, the fraction of high-angle grain boundaries (HAGBs) with the misorientation tolerance angles (MTAs) greater than 15° reduced, while the mean equivalent diameter, MED_MTA≥15°, of ferrite grains with HAGBs increased. Accordingly, the impact toughness of WM was degraded from 108.1 J to 39.4 J with the increase in Si. The increase in M/A constituents and inclusions size reduced the critical fracture stress, thereby formation of larger microcracks and cleavage planes occurred. The reduced HAGBs exhibited a low hindering effect on crack propagation, and, consequently, the impact toughness decreased with increasing Si content.