High purity titanium (Ti) thin strip was prepared by rolling with large deformation and was characterized by the means of Transmission Electron Microscopy (TEM), selected area diffraction (SAED) pattern, high-resolution (HRTEM) analysis, as well as Transmission Kikuchi Diffraction (TKD). It is found that there are face-centered cubic (FCC) Ti laths formed within the matrix of hexagonal close packing (HCP) Ti. This shows that the HCP-FCC phase transition occurred during the rolling, and a specific orientation relationship (OR) between HCP phase and FCC phase obeys ⟨0001⟩_α// ⟨001⟩_FCC and {100}_α//{110}_FCC. The ORs of HCP-FCC phase transition are deeply studied by TKD pole figure and phase transformation matrix. It is found that the derived results via pole figure and transformation matrix are equivalent, and are consistent with TEM-SAED analysis results, which proves that these two methods can effectively characterize the ORs of HCP-FCC phase transition and predict possible FCC phase variants.

Pearlitic steel rods are subjected to cold-drawing processes to produce pearlitic steel wires with true strains ranging from 0.81 to 2.18. Tensile tests are utilized to attain mechanical properties of cold-drawn pearlitic steel wires. TEM and XRD investigations were performed on the microstructure of the cold-drawn steel wires. With an increasing cold-drawn strain, both the interlamellar spacing and cementite lamellae thickness decrease, while the dislocation density significantly increases. The drawn wire has a tensile strength of 2170 MPa when the true stain reaches 2.18. Deformation-induced cementite dissolution occurs during cold-drawing progress, which releases many C atoms. The findings indicate that the supersaturation of C is heterogeneously distributed in the ferrite matrix. The ordered distribution of the released C in ferrite phases creates short-range order (SRO). SRO clusters and disordered Cottrell atmospheres contribute to solution strengthening, which, together with dislocation strengthening and interlamellar boundary strengthening, form an effective strengthening mechanism in cold-drawn pearlitic steel wires. Our work provides new insights into carbon redistribution and the mechanism of solution strengthening within ferrous phases.