Magnetic microwires can present excellent soft magnetic properties and a giant magnetoimpedance effect. In this paper, we present our last results on the effect of postprocessing allowing optimization of the magnetoimpedance effect in Co-rich microwires suitable for magnetic microsensor applications. Giant magnetoimpedance effect improvement was achieved either by annealing or stress-annealing. Annealed Co-rich presents rectangular hysteresis loops. However, an improvement in magnetoimpedance ratio is observed at fairly high annealing temperatures over a wide frequency range. Application of stress during annealing at moderate values of annealing temperatures and stress allows for a remarkable decrease in coercivity and increase in squareness ratio and further giant magnetoimpedance effect improvement. Stress-annealing, carried out at sufficiently high temperatures and/or stress allowed induction of transverse magnetic anisotropy, as well as magnetoimpedance effect improvement. Enhanced magnetoimpedance ratio values for annealed and stress-annealed samples and frequency dependence of the magnetoimpedance are discussed in terms of the radial distribution of the magnetic anisotropy. Accordingly, we demonstrated that the giant magnetoimpedance effect of Co-rich microwires can be tailored by controlling the magnetic anisotropy of Co-rich microwires, using appropriate thermal treatment.

Applications in security and electronic surveillance require a combination of excellent magnetic softness with good mechanical and anticorrosive properties and low dimensionality. We overviewed the feasibility of using glass-coated microwires for electronic article surveillance and security applications, as well as different routes of tuning the magnetic properties of individual microwires or microwire arrays, making them quite attractive for electronic article surveillance and security applications. We provide the routes for tuning the hysteresis loops’ nonlinearity by the magnetostatic interaction between the microwires in the arrays of different types of amorphous microwires. The presence of neighboring microwire (either Fe- or Co-based) significantly affects the hysteresis loop of the whole microwires array. In a microwires array containing magnetically bistable microwires, we observed splitting of the initially rectangular hysteresis loop with a number of Barkhausen jumps correlated with the number of magnetically bistable microwires. Essentially, nonlinear and irregular hysteresis loops have been observed in mixed arrays containing Fe- and Co-rich microwires. The obtained nonlinearity in hysteresis loops allowed to increase the harmonics and tune their magnetic field dependencies. On the other hand, several routes allowing to tune the switching field by either postprocessing or modifying the magnetoelastic anisotropy have been reviewed. Nonlinear hysteresis loops have been also observed upon devitrification of amorphous microwires. Semihard magnetic microwires have been obtained by annealing of Fe–Pt–Si microwires. The observed unique combination of magnetic properties together with thin dimensions and excellent mechanical and anticorrosive properties provide excellent perspectives for the use of glass-coated microwires for security and electronic surveillance applications.

We study the effect of annealing and the applied magnetic field from 50 Oe to 20 kOe on the magneto-structural behavior of Ni₂FeSi-based Heusler microwires fabricated by using Taylor-Ulitovsky technique. Using the XRD analysis, a strong effect of annealing, manifested as the development of the crystallization process, was observed. The average grain size and crystalline phase content of annealed sample increase from 21.3 nm and 34% to 32.8 nm and 79%, respectively, as-compared to the as-prepared one. In addition, upon annealing, phase transforms into a monoclinic martensitic structure with a modulation of 10 M, which cannot be found in the as-prepared sample. Concerning the magnetic properties, both samples show ferromagnetic behavior below and above the room temperature, where the Curie temperature of Ni₂FeSi is higher than the room temperature. The induced secondary phases have a noticeable effect on the magnetic behavior of the annealed sample, where a high normalized saturation magnetization (NM_s) and low normalized reduced remenance (M_r = M/M_5K), compared to the as-prepared have been detected. Additionally, the coercivity of annealed sample shows one flipping point at 155 K where its behavior changes with temperature. Meanwhile, the as-prepared sample show two flipped point at 205 K and 55 K. A mismatch between field cooling (FC) and field heating (FH) magnetization curves with temperature has been detected for annealed sample at low applied magnetic field. The difference in magnetic and structure behavior of Ni₂FeSi microwires sample is discussed considering the effect of induced internal stresses by the presence of a glass coating and the recrystallization and stresses relaxation upon annealing.

Magnetoimpedance (MI) response of near-zero magnetostriction Co-based amorphous ribbons exhibiting a macroscopic uniaxial magnetic anisotropy induced by stress-annealing (300 MPa at 340, 360, and 400 °C during 1 h) is investigated in a frequency range from 10 MHz up to 1000 MHz. Comparison among MI effect of these stress-annealed ribbons with that previously reported in ribbons with similar composition in as-cast state is discussed. It is remarkable that a more spectacular and defined MI effect is observed in the stress-annealed ribbons owing to the presence of a macroscopic uniaxial transverse magnetic anisotropy developed with the stress annealing which enhances the transverse component of the magnetic susceptibility. The influence of a preceding stress relief before the stress-annealing process on the MI effect is also analyzed.

Martensitic transition and magnetic response of Ni_50−x Pd_x,y Mn₃₆ Sn_14−y (x = 0, 1, 2 and y = 0, 1) Heusler alloys were analysed. The crystalline structure of each composition was solved by X-ray diffraction pattern fitting. For x = 1 and 2, the L2₁ austenite structure is formed and, for y = 1, the crystallographic phase is a modulated martensitic structure. From differential scanning calorimetry scans, we determine characteristic transformation temperatures and the entropy/enthalpy changes. The temperatures of the structural transformation increase with the addition of Pd to replace Ni or Sn, whereas the austenitic Curie temperature remains almost unvarying. In addition, the magneto-structural transition, investigated by magnetic measurements, is adjusted by suitable Pd doping in the alloys. The peak value of the magnetic entropy changes reached 4.5 J/(kg K) for Ni₅₀Mn₃₆Sn₁₃Pd₁ (external field: 50 kOe).

Stress-annealing enabled a considerable improvement in the GMI effect in both Fe- and Co-rich glass-coated microwires. Additionally, a remarkable magnetic softening can be achieved in stress-annealed Fe-rich microwires. Observed stress-annealing induced magnetic anisotropy is affected by annealing conditions (temperatures and stresses applied during annealing). The highest GMI ratio up to 310% was obtained in stress-annealed Co-rich microwires, although they presented rectangular hysteresis loops. A remarkable magnetic softness and improved GMI ratio over a wide frequency range were obtained in stress-annealed Fe-rich microwires. Irregular magnetic field dependence observed for some stress-annealing conditions is attributed to the contribution of both the inner axially magnetized core and outer shell, with transverse magnetic anisotropy.