Na⁺-conducting, binary electrolytic mixtures, based on 1-ethyl-3-methyl-imidazolium, trimethyl-butyl-ammonium, and N-alkyl-N-methyl-piperidinium ionic liquid (IL) families, were designed and investigated. The anions were selected among the per(fluoroalkylsulfonyl)imide families. Sodium bis(trifluoromethylsulfonyl)imide, NaTFSI, was selected as the salt. The NaTFSI-IL electrolytes, addressed to safer sodium battery systems, were studied and compared in terms of ionic conductivity and thermal stability as a function of the temperature, the nature of the anion and the cation aliphatic side chain length. Room temperature conductivities of interest for sodium batteries, i.e., largely overcoming 10⁻⁴ or 10⁻³ S cm⁻¹, are displayed. Similar conduction values are exhibited by the EMI-based samples even below −10 °C, making these electrolyte mixtures potentially appealing also for low temperature applications. The NaTFSI-IL electrolytes, with the exception of the FSI-ones, are found to be thermally stable up to 275 °C, depending on the nature of the cation and/or anion, thus extending their applicability above 100 °C and remarkably increasing the reliability and safety of the final device, especially in the case of prolonged overheating.

In this work a purification route of precursors for ionic liquids tailored to electrochemical energy storage systems is reported and described. The study was carried out on the N-butyl-N-methylpyrrolidinium bromide (PYR₁₄Br) precursor, which represents the intermediate product of the synthesis process of the N-butyl-N-methylpyrrolidinium bis(trifluoromethanesulfonyl)imide (PYR₁₄TFSI) hydrophobic ionic liquid. The target is to develop an easy and cost-effective approach for efficiently purifying several kinds of ionic liquid precursors and determining their purity content. The PYR₁₄Br precursor was synthesized through an eco-friendly preparation procedure, which requires water as the only processing solvent, and purified through sorbent materials, such as activated charcoal and alumina. The effect of the treatment/nature/content of sorbents and processing temperature/time was investigated. The impurity content was detected by UV-VIS spectrophotometry measurements. Additionally, a correlation between the measured absorbance and the content of impurities within the precursor was obtained. The purity level of the precursor was seen to play a key role in the electrochemical performance of the ionic liquids.