High Speed Sintering (HSS) is an additive manufacturing process with great potential to produce complex, high-quality polymer parts on an industrial scale. However, little information is currently available on the characteristics of the powder materials used and the part properties that can be achieved. This is also the case for the standard material polyamide 12 (PA 12) and the first commercially available HSS machine, the VX200 HSS. The aim of this study is, therefore, to provide the first comprehensive overview of the properties of PA 12 parts manufactured with the VX200 HSS and the characteristics of the PA 12 powder. This includes the analysis of the influence of part orientation and part position in the build job. To characterize the powder, particle size distribution, particle shape, thermal properties and powder flowability were analyzed. To characterize the parts, density and various thermal, mechanical and geometrical properties were analyzed. In summary, the powder material and part properties are largely similar to those of other Powder Bed Fusion of Polymer (PBF/P) processes. However, there are also significant differences for some part properties. It was also determined that the anisotropy of parts is very low compared to that of many other additive manufacturing processes.

In the power industry, various electrically insulating materials are used to ensure proper mechanical, thermal, and dielectric performance over decades of equipment operation. In power transformers, cellulose is the predominant material in manufacturing various insulation components. Most of these products are manufactured by wet-molding technology. However, this process is long, labor-intensive, and highly energy-demanding. Under the frame of an EU-funded grant, a new kind of insulation material and manufacturing process were developed. Fully bio-based material (produced in the form of pellets) can be processed using additive manufacturing, allowing for much shorter manufacturing times for insulation products, with considerably less scrap and energy consumption (due to the elimination of the drying stage). The focus of the project was extrusion additive manufacturing technology, but at a later stage, a biomaterial powder was developed, making it possible to print with other technologies. In the paper, comparative studies on various additive manufacturing techniques of newly developed biopolymers have been presented, including extrusion, High Speed Sintering (HSS), and Selective Laser Sintering (SLS). The applicability of such material in power transformers required extensive testing of various properties. These results are discussed in the paper and include: oil compatibility, volume resistivity measurements, permittivity and dissipation factor measurements, determination of partial discharge inception voltage, partial discharges measurement, and breakdown voltage measurements. Although mechanical properties remain below industrial targets, the pioneering results provide a promising route for unique directions toward more sustainable manufacturing of high-voltage cellulose insulation and ideas for improving the material properties during the printing process.