UJM-1P is the 7^th MWW zeolite structure obtained by direct synthesis.

A novel experimental technique, quasi-equilibrated temperature-programmed desorption and adsorption (QE-TPDA), was used to study the water sorption properties and hydrothermal stability of aluminum trimesate MIL-96 and aluminum isophthalate CAU-10, which have been selected due to their remarkable sorption properties. The QE-TPDA profiles of water observed for MIL-96 and CAU-10 confirmed the hydrophilic nature of these materials. Complex QE-TPDA profiles indicate that water sorption in MIL-96 follows a three-step pore filling mechanism. The shape of single desorption peaks in the QE-TPDA profiles for CAU-10 confirms that water sorption involves a reversible phase transition. Based on the QE-TPDA profiles, the water adsorption heat was determined: 45–46 kJ/mol for CAU-10 and 43–56 kJ/mol for MIL-96, in the latter case depending on the adsorption extent. Hydrothermal stability tests revealed that MIL-96 retained its stable porosity-related sorption capacity for water after hydrothermal treatment up to 290 °C. Gradual changes in the QE-TPDA profiles due to the hydrothermal treatment above 290 °C, with decreasing the high-temperature desorption peak and increasing the low-temperature one, indicate minor structural changes occurring in this material. Only after 410 °C treatment was fast degradation of MIL-96 observed. CAU-10 exhibited high and unchanged hydrothermal stability up to 400 °C.

The present studies were conducted to show the potential of 2D zeolites as effective and non-toxic carriers of drugs. Layered zeolites exhibit adjustable interlayer porosity which can be exploited for controlled drug delivery allowing detailed investigation of the drug release because the structure of the carrier is known exactly. This study was conducted with model drugs ciprofloxacin and piracetam, and ZSM-55 with ca 1 nm thick layers, in detemplated and pillared forms. The release profiles differed from the commercial, crystalline forms of drugs—the release rate increased for ciprofloxacin and decreased for piracetam. To understand the dissolution mechanisms the release data were fitted to Korsmeyer-Peppas equation, showing Fickian (for pillared) and anomalous (for detemplated sample) transport. FT-IR studies showed that strong interaction carrier-drug may be responsible for the modified, slowed down release of piracetam while better solubility and faster release of ciprofloxacin was attributed to formation of the protonated form resulting in weaker interaction with the zeolite than in the pure crystalline form. Two independent tests on L929 mice fibroblasts (ToxiLight and PrestoBlue) showed that ZSM-55, in moderate concentrations may be safely used as a carrier of drug molecules, not having negative effect on the cells viability or proliferation rate.

MWW type zeolites are characterized by the presence of zeolitic layers of 2.5 nm thickness, containing 10-member ring sinusoidal channels inside and supercavities with 12-member ring openings located on their surfaces. Expansion and pillaring of layered zeolites increase the access to active sites and can enable or facilitate catalytic activity towards larger reactant molecules. This goal is explored in this work reporting the pillaring of layered zeolite MCM-56 with MWW topology by tetraethylorthosilicate (TEOS) treatment with the assistance of isopropanol, aimed at obtaining hierarchical micro-mesoporous systems. MCM-56 (Si/Al = 12) was synthesized with hexamethyleneimine as a structure-directing and aniline as a structure-promoting agent. Hierarchical porous systems were obtained using two different pillaring methods: (1) with TEOS only and (2) with TEOS mixed with isopropanol. The MWW framework was preserved during swelling/pillaring in both methods. Pillared zeolites obtained via alcohol-assisted pillaring possessed unique intermediate micro-mesopores with the size of about 2 nm. IR study revealed a decrease in the concentration of accessible acid centers upon pillaring. However, the fraction of acid sites on the external surface, accessible for adsorption of large molecules, increased by up to 90%. Catalytic activity was evaluated in the Friedel-Crafts alkylation of mesitylene with benzyl alcohol. Pillaring resulted in reduction of the acid site concentrations, but the materials retained high catalytic activity. Pillaring in the presence of alcohol produced increased turnover frequency values based on the concentrations of the external acid sites.