Nanostructured TiO₂ is one of the best materials for photocatalysis, thanks to its high surface area and surface reactivity, but its large energy bandgap (3.2 eV) hinders the use of the entire solar spectrum. Here, it is proposed that defect‐engineered nanostructured TiO₂ photocatalysts are obtained by hydrogenation strategy to extend its light absorption up to the near‐infrared region. It is demonstrated that hydrogenated or colored TiO₂ hollow spheres (THS) composed of hierarchically assembled nanoparticles result in much broader exploitation of the solar spectrum (up to 1200 nm) and the engineered surface enhances the photogeneration of charges for photocatalytic processes. In turn, when applied for photodegradation of a targeted drug (Ciprofloxacin) this results in 82% degradation after 6 h under simulated sunlight. Valence band analysis by photoelectron spectroscopy revealed the presence of oxygen vacancies, whose surface density increases with the hydrogenation rate. Thus, a tight correlation between degree of hydrogenation and photocatalytic activity is directly established. Further insight comes from electron paramagnetic resonance, which evidences bulk Ti³⁺ centers only in hydrogenated THS. The results are anticipated to disclose a new path toward highly efficient photocatalytic titania in a series of applications targeting water remediation and solar fuel production.

This review article summarizes the synthesis and the fluorescence mechanism together with the most important applications in thermometry, bio-imaging, LSCs and photocatalysis of red/near-infrared C-dots.

Environmental pollution is a complex problem that threatens the health and life of animal and plant ecosystems on the planet. In this respect, the scientific community faces increasingly challenging tasks in designing novel materials with beneficial properties to address this issue. This study describes a simple yet effective synthetic protocol to obtain nickel hexacyanoferrate (Ni‐HCF) nanocubes as a suitable photocatalyst, which can enable an efficient photodegradation of hazardous anthropogenic organic contaminants in water, such as antibiotics. Ni‐HCF nanocubes are fully characterized and their optical and electrochemical properties are investigated. Preliminary tests are also carried out to photocatalytically remove metronidazole (MDZ), an antibiotic that is difficult to degrade and has become a common contaminant as it is widely used to treat infections caused by anaerobic microorganisms. Under simulated solar light, Ni‐HCF displays substantial photocatalytic activity, degrading 94.3% of MDZ in 6 h. The remarkable performance of Ni‐HCF nanocubes is attributeto a higher ability to separate charge carriers and to a lower resistance toward charge transfer, as confirmed by the electrochemical characterization. These achievements highlight the possibility of combining the performance of earth‐abundant catalysts with a renewable energy source for environmental remediation, thus meeting the requirements for sustainable development.

Cerium‐containing titania nano‐octahedra (CeTNOh) are obtained by ultrasonication‐hydrothermal synthesis of Ce‐containing titanate nanowires (0.35, 0.46, and 0.70 Ce mol %) from commercial TiO2 (Degussa P25). CeTNOh are tested as photocatalysts to degrade a target pollutant (ciprofloxacin) under simulated solar light and at mild conditions. CeTNOh are anatase polymorphs with increasing crystallite size as Ce content increases. Hydrothermal treatments enhance the specific surface area (SSA) compared to P25, although Ce addition slightly reduces SSA while increasing crystallite size. Electron Microscopy confirms the morphology, although higher Ce levels hinder a full transformation. X‐ray photoemission spectroscopy (XPS) shows the presence of Ce³⁺/Ce⁴⁺ redox pair, promoting electron mobility and Ti‐Ce interactions. Optical and electronic spectroscopy reveals that Ce loading reduces the bandgap from 3.20 to 2.74 eV, extending light absorption into the visible range, thus enhancing the photocatalytic activity. The best sample, CeTNOh0.35, achieved 83% degradation of ciprofloxacin after 360 minutes under solar irradiation, with poor adsorption in the dark period. Higher Ce loadings negatively affect photoactivity by partially covering titania active sites. Reusability tests confirm the stability and efficiency of CeTNOh0.35 over three cycles, highlighting the importance of octahedral morphology in Ce‐containing systems to boost the final photoactivity for water remediation.

Cerium-doped titania nanoflowers are obtained by hydrothermal synthesis, with different amounts of cerium (0.3, 0.5, and 1.0 at%). Both undoped nanoflowers (TNF) and Ce-doped TNF (Cex) are tested as photocatalysts in the degradation of the target pollutant (metronidazole) under simulated solar light. The samples are rutile polymorphs with high crystallinity and present a nanoflower-like morphology of about 1 µm in diameter and are made up of nanoscale petals (in the range of 100–300 nm). EDX spectroscopy was coupled with SEM and performed on the Ce-doped samples to determine the elemental composition of the catalysts and the Ce distribution in each sample. Optical and electronic spectroscopies reveal that Ce loading narrows the band gap from 3.0 to 2.8 eV, extending light absorption into the visible range of the spectrum and thus enhancing the photocatalytic activity. The best sample, Ce1, achieved 67% degradation of metronidazole after 360 min under solar irradiation at pH 4, compared to bare TNF, which reached 35%. Reusability tests confirm the chemical stability and photocatalytic efficiency of Ce1 over three cycles, and free-radical trapping experiments confirmed ·O₂⁻ and ·OH as major active species in metronidazole degradation. This study highlights the synergistic impact of morphology and doping on solar-driven organic pollutant degradation.