The chlorophyll fluorescence (F) temperature curves in a linear time-temperature heating/cooling regime were used to study heat-induced irreversible F changes in primary green leaves of spring barley (Hordeum vulgare L. cv. Akcent). The leaf segments were heated in a stirred water bath at heating rates of 0.0083, 0.0166, 0.0333, and 0.0500 °C s⁻¹ from room temperature up to maximal temperature T _m and then linearly cooled to 35 °C at the same rate. The F intensity was measured by a pulse-modulated technique. The results support the existence of the two critical temperatures of irreversible F changes postulated earlier, at 45–48 and 53–55 °C. The critical temperatures are slightly dependent on the heating rate. Two types of parameters were used to characterize the irreversibility of the F changes: the coefficient of irreversibility μ defined as the ratio of F intensity at 35 °C at the starting/ending parts of the cycle and the slopes of tangents of linear parts of the F temperature curve. The dependence of μ on T _m revealed a maximum, which moved from 54 to 61 °C with the increasing heating/cooling rate v from 0.0083 to 0.0500 °C s⁻¹, showing two basic phases of the irreversible changes. The Arrhenius and Eyring approaches were applied to calculate the activation energies of the initial increase in μ. The values varied between 30 and 50 kJ mol⁻¹ and decreased slightly with the increasing heating rate.

It is widely known that glass–epoxy laminates are renowned for their high stiffness, good thermal properties, and economic qualities. For this reason, composite materials find successful applications in various industrial sectors such as aerospace, astronautics, the storage sector, and energy. The aim of this study was to investigate the mechanical and thermal properties of composite materials comprising two different types of epoxy resin and three different hardeners, both at room temperature and under cryogenic conditions. The samples were produced at IZOERG (Gliwice, Poland) using a laboratory hot-hydraulic-press technique. During cyclic loading–unloading tests, degradation up to a strain level of 0.6% was observed both at room temperature (RT) and at 77 K. For a glass-reinforced composite with YDPN resin (EP_1_1), the highest degradation was recorded at 18.84% at RT and 33.63% at 77 K. We have also investigated the temperature dependence of thermal conductivity for all samples in a wide temperature range down to 5 K. The thermal conductivity was found to be low and had a relative difference of up to 20% among the composites. The experimental results indicated that composites under cryogenic conditions exhibited less damage and were stiffer. It was confirmed that the choice of hardener significantly influenced both properties.