An improved method for producing high-purity quartz (Qtz) and potassium feldspar (Kfs) concentrates was developed using various chemical reagents. Froth flotation experiments on a Qtz–Kfs mixture showed that quartz could be selectively floated from Kfs in diluted hydrofluoric acid (HF) using a frother. Similarly, feldspar could be selectively floated from quartz. Recovery rates depended on reagent choice, pH levels, HF modifier dosage, and HF conditioning time. High recoveries and good grades were achieved for both quartz and feldspar at low pH levels. Among the five collectors tested, Brij C20 showed the highest recovery when used in conjunction with HF and a frother alone and a concentrate containing 82.8% quartz was obtained at a 96% recovery rate. Good recoveries were also achieved with collectors like Duomeen C and Flotigam V4343 for floating K-feldspar, with a Kfs concentrate of 99.9% purity at a 94% recovery. Lilaflot OT 55 and Duomeen TDO were less effective. The concentration of HF was 22 kg/t, which implies an important reduction with respect to the earlier research.

An approach for the remediation of heavy metal-contaminated wastewater that is gaining increasing attention is the application of hydroxyapatite (HAP)-based particles. HAP is conventionally synthesized through wet chemical precipitation of calcium and phosphate ions, although later studies have focused on HAP synthesis from solid calcite contacted with a phosphate solution under ambient conditions. This synthesis route can allow saving soluble Ca-chemicals and, thus, make the process more cost-efficient. The aim of this study was to coat natural calcite powder with a layer of HAP for the removal of Zn and Cu from contaminated water. For this purpose, a HAP layer was synthesized on calcite particles, characterized using several complementary techniques and evaluated for the removal of Zn and Cu from synthetic solutions. Sorption kinetics and equilibrium isotherms, as well as the effect of sonication of the synthesized sample on its sorption performance, were determined. The results showed that calcite particles were efficiently coated with a HAP layer with high capacity in removing Zn and Cu from acidic solutions, with a q_max of 34.97 mg/g for Zn (increased to 37.88 g/mg after sonication of the sample) and 60.24 mg/g for Cu (which hardly varied with sonication). The mechanisms behind the sorption of Zn and Cu onto HAP, inferred from pH changes, the relation between metal uptake and Ca²⁺ release and XRD analysis, included surface complexation, ion exchange and precipitation of new Zn- and Cu-containing phases.

The paper presents a comparison of the concentration methods conventional jig, air jig, and sensor-based sorting to treat construction and demolition waste. All tests were made with concrete, brick, and gypsum particles and the tests aim to separate these materials into different size ranges, depending on the method. The equipment tested, conventional jig, air jig, and sensor-based sorting present good results to concentrate construction and demolition waste particles, with different concentrations and mass recoveries. The results show particularly good mass recoveries and particle concentration for conventional jig, especially for concrete and gypsum particles. Sensor-based sorting should preferably use concentration circuits for best results.