The effect of alkali metal (Li, Na, K) incorporation on the morphology and water vapor uptake properties of mesoporous Al₂O₃ has been studied. The modification of the raw material, pseudoboehmite, represented a mixture of low-temperature phases (γ + η + χ)-Al₂O₃, and has been done at low-temperature that does not change the phase ratio. A decrease in specific surface values and an average pores size increase were observed as a result of the introduction of metal cations by impregnation and subsequent thermal treatment. The influence of the content of the modifying metal on the adsorption ability of the obtained samples in relation to water vapours has been studied. It has been established that alkaline modification Al₂O₃ with the lithium cations did not result in adsorption ability improvement, whereas samples that were modified with sodium or potassium in the amount of 1.2 weight % and 2.6 weight %, respectively, possess a higher equilibrium capacity (by ~40%), as compared to that of the initial sample (Al₂O₃), and a sufficiently high adsorption rate.

The review describes the main methods of obtaining hydroxides and aluminium oxides (AO) of various structures from gibbsite. The promising techniques of obtaining AO adsorbents are discussed, namely the technique of thermal activation in the mode of pneumatic transport with gibbsite by heated air (TCA Gb) and the technique of thermal activation of gibbsite in centrifugal flash reactors (CTA Gb). The main methods of improving the adsorbent properties of AO, such as the optimisation of texture characteristics and phase composition, as well as the influence of the modification of aluminium oxide adsorbents, obtained using CTA and TCA technologies with cations of alkaline metals, are considered. It is shown that the modification allows a controlled variation of the characteristics of donor and acceptor active sites on the surface of adsorbents and, thus, a substantial increase in their adsorption activity, in particular, with respect to water vapour.

Fundamental dynamic (kinetic) aspects of the process in which water vapor interacts with the surface of drying agents that are synthesized on the basis of low-temperature modification of aluminum...

To establish principal regularities of the hydrotreatment of rapeseed oil fatty acid triglycerides (FATs), the kinetics of this process has been studied at temperatures of 300–380°C, contact times of 0.38–0.10 h, and a hydrogen pressure of 1.0 MPa in a flow fixed-bed reactor. The process is performed over nonsulfided nickel catalysts, which are of great practical interest for the production of green diesel. The kinetic scheme of the process with consideration for target products (alkanes) and all oxygen-containing by-products has been proposed. The quantitative estimate, which enables the prediction of the composition of products for other process conditions, has been obtained for the principal paths of the hydrotreatment of rapeseed oil FATs.

The dynamic capacity of the commercial desiccant (NaX zeolite) and the adsorbent, synthesised based on low-temperature modifications of aluminium oxide, obtained from bayerite-containing hydroxide, was determined with respect to water vapour. Experimental studies were carried out using a pilot installation at the atmospheric pressure and increased pressure (up to 0.6 MPa) and high humidity. The increase in the height of the layer of the adsorbents leads to an increase of their dynamic capacity with respect to water vapour and the protective power (action) time of the layer. It was shown that at the atmospheric pressure and the pressure of up to 0.3 MPa, the dynamic capacity of NaX is greater; at a higher pressure, the adsorption capacity of the developed adsorbent Al₂O₃ becomes greater than the zeolite capacity, which allows recommending it as a desiccant at increased pressure.