An all-silica photonic bandgap fiber with a cladding index difference of approximately 2 % and diameter-to-pitch ratio (d/Λ) of 0.12 was fabricated and studied. To our knowledge, this is the first report on the properties of photonic bandgap fiber with such a small d/Λ. The fiber is single-mode in the fundamental bandgap. The mode field diameter in the 1000-1200 nm wavelength range is 19-20 μm. The minimum loss in the same range is 20 dB/km for a 30-cm bending diameter. In our opinion, all-silica photonic bandgap fiber can serve as a potential candidate for achieving single-mode propagation with a large mode area.

A design of a polarizing all-glass Bragg fiber with a microstructure core has been proposed for the first time. This design provides suppression of high-order modes and of one of the polarization states of the fundamental mode. The polarizing fiber was fabricated by a new, simple method based on a combination of the modified chemical vapor deposition (MCVD) process and the rod-in-tube technique. The mode field area has been found to be about $870{\mathrm{\mu m}}^2$ near $\lambda =1064\mathrm{nm}$. The polarization extinction ratio better than $13\mathrm{dB}$ has been observed over a 33% wavelength range (from 1 to $1.4\mathrm{\mu m}$) after propagation in a $1.7\mathrm{m}$ fiber piece bent to a radius of $70\mathrm{cm}$.

A bismuth-doped-pure-silica holey fiber is fabricated using a fiber preform made by the furnace chemical vapor deposition method. The spectroscopic properties of the fiber are studied, and laser action at $\lambda =1450\mathrm{nm}$ with an efficiency of 12% is demonstrated.

The paper presents the results of theoretical and experimental studies of all-glass leakage channel microstructured optical fibers (MOFs) with a large mode area and low bending losses. These MOFs contain two layers of fluorine-doped silica glass elements with a reduced refractive index, different diameters, and different distances between them. A numerical analysis of the properties of these MOFs was performed using the finite element method. The leakage losses for the fundamental and higher-order modes were calculated in the spectral range from 0.65 μm to 1.65 μm. Simulation results show that the proposed MOF design allows for single-mode guidance in the spectral range from 0.92 μm to 1.21 μm with a bending radius of down to 0.08 m. The measured losses of the fabricated MOF with a core diameter of 22.5 μm and a bending radius of 0.1 m were less than 0.1 dB/m in the spectral range from 0.9 μm to 1.5 μm. It is demonstrated that the segments of this MOF longer than 5 m are single-mode.