Research in historical timber assessment is hindered by the limited availability of samples, yet understanding the fire resistance of historic wood is crucial for preservation efforts. There is an opinion that historic wood behaves similarly to contemporary wood in terms of fire resistance. The aim of this paper is to observe the rate of charring of historical pine wood during the experiment, the color changes in the sample that occurred due to thermal loading, and the changes in the chemical composition of pine wood. Test samples made from historic pine wood were loaded with a 50 kW∙m⁻² radiation panel for 60 min. The charring process was faster at the beginning of the charred layer formation. The charring rate at the beginning of the test at a depth of 10 mm from the exposed side reached values from 1.28 mm∙min⁻¹ to 3.16 mm∙min⁻¹. At a depth of 30 mm from the exposed side, the individual charring rates approached a value of 1 mm∙min⁻¹ (0.99 mm∙min⁻¹ to 1.08 mm∙min⁻¹). Observations during medium-scale testing revealed distinct layers forming on the exposed side: a charred layer, charring base, pyrolysis layer, and intact wood. The chemical composition of the wood changed under the influence of the thermal load. The relative contents of extractives and holocellulose decreased with the increasing temperature while the lignin content increased. The highest value of combustion heat was measured in the charred layer of the sample. Correlation analysis demonstrated a negative relationship between the combustion heat and holocellulose, while a positive correlation was found with the lignin content. Chemical changes were also monitored using the FTIR method. These findings provide valuable insights into the behavior of historic pine wood under thermal loading, which is essential for understanding and preserving historical structures.

There is a vast diversity of historic heirloom apple varieties around the world. Apples of various colors, sizes, tastes, uses, and ripening times can be found. In Slovakia, there has recently been a rising interest to preserve these apple varieties. The life of a tree is partially influenced by the growing conditions of the environment where the tree grows. In this paper, macroscopic and microscopic characteristics of four selected heirloom apple trees growing in Slovakia’s Štiavnické vrchy were observed. Studying the microscopic structure of historical heirloom apple trees wood could reveal specific cell arrangements of tissues. This could help to specify the individual varieties.

Gap dynamics are driving many important processes in the development of temperate forest ecosystems. What remains largely unknown is how often the regeneration processes initialized by endogenous mortality of dominant and co-dominant canopy trees take place. We conducted a study in the high mountain forests of the Central Western Carpathians, naturally dominated by the Norway spruce. Based on the repeated forest inventories in two localities, we quantified the structure and amount of deadwood, as well as the associated mortality of standing dead canopy trees. We determined the basic specific gravity of wood and anatomical changes in the initial phase of wood decomposition. The approach for estimating the rate of gap formation and the number of canopy trees per unit area needed for intentional gap formation was formulated based on residence time analysis of three localities. The initial phase of gap formation (standing dead tree in the first decay class) had a narrow range of residence values, with a 90–95% probability that gap age was less than 10 or 13 years. Correspondingly, a relatively constant absolute number of 12 and 13 canopy spruce trees per hectare died standing in 10 years, with a mean diameter reaching 50–58 cm. Maximum diameters trees (70–80 cm) were represented by 1–4 stems per hectare. The values of the wood-specific gravity of standing trees were around 0.370–0.380 g.cm⁻³, and varied from 0.302 to 0.523 g.cm⁻³. Microscopically, our results point out that gap formation is a continuous long-lasting process, starting while canopy trees are living. We observed early signs of wood degradation and bacteria, possibly associated with bark beetles, that induce a strong effect when attacking living trees with vigorous defenses. New information about the initial phase of gap formation has provided a basis for the objective proposal of intervals and intensities of interventions, designed to promote a diversified structure and the long-term ecological stability of the mountain spruce stands in changing climate conditions.

Previous phytopathological studies of the fungal pathogen Nectria cinnabarina have been focused on its distribution and host diversity but little is known about the spread of this pathogen and the defence responses of forest trees to an infection inside host tissues. Histopathological alterations of bark, periderm, phloem and woody tissues were investigated in sycamore maple (Acer pseudoplatanus) branches following their natural attack by the advanced anamorph and teleomorph developmental stages of the fungus. Light, fluorescence, confocal laser scanning and scanning electron microscopy techniques supplemented by X-ray micro-computed tomography imaging were used to distinguish between healthy and disintegrated plant tissues. The intercellular spread of fungal hyphae was found primarily in the phelloderm. Expanding hyphae aggregations produced ruptures in the phellem and the disintegration of both phellogen and phellodermal parenchyma cells in close proximity to the expanding fruiting bodies of the fungus. Thicker hyphae of the teleomorph fungal stage heavily disintegrated the phelloderm tissues and also induced enhanced sclerification of the nearby phloem tissues that limited the spread of the infection into the sieve tubes. Both the intercellular and intracellular spread of hyphae inside the peripheral parts of sclereid clusters led to the disintegration of the compound middle lamellae but the hyphae were only rarely able to pass through these structural phloem barriers. The massive fungal colonization of both lumens and disintegrated tangential cell walls of ray parenchyma cells resulted in severe cambial necroses. Although the hyphae penetrated into the outermost annual growth rings of the xylem, no cell wall disintegration of the parenchyma cells, vessels and fibres was revealed. Despite the local cambial necroses and severe phloem ray disintegration, the bark remained attached to the examined branches and no bark cankers were formed.

The rate of pulping of spruce wood depends on the pretreatment of wood chips. Current pretreatment methods that are being investigated and applied appear to be time-consuming and energy intensive. These drawbacks can be minimized by pretreating the chips through compression, perpendicular to the fibre direction. In the maceration process, it is currently very difficult to measure pulp characteristics in real time; therefore, different treatment times were selected for uncompressed and compressed chips. Maceration was carried out by boiling the chips in a solution of acetic acid and hydrogen peroxide mixed in a 1:1 ratio. Subsequently, the colour and lignin content of the maceration product were measured to demonstrate the accelerated maceration of compressed chips compared with uncompressed ones. The colour of the product obtained from compressed chips after 25 min of pulping was similar to that of holocellulose, while the lignin content was at the detection limit. Given the same pulping time, the product obtained from uncompressed chips was darker, more saturated, and contained a significantly higher amount of lignin. The compression of wood chips proved to be a promising pretreatment method for accelerating the maceration of spruce wood.