To expand the applicability of gel fracturing fluids in ultra-high-temperature reservoirs, a temperature-resistant polymer was synthesized using the solution polymerization method. Subsequently, an ultra-high-temperature-resistant polymer gel was formulated by incorporating an organic zirconium crosslinking agent. A comprehensive investigation was carried out to systematically study and evaluate the steady shear property, dynamic viscoelasticity, and temperature and shear resistance performance, as well as the core damage characteristics of the polymer gel. The obtained results demonstrate that the viscosity remained at 147 mPa·s at a temperature of 200 °C with a shear rate of 170 s⁻¹. Compared with the significant 30.9% average core damage rate observed in the guanidine gum fracturing fluid, the core damage attributed to the polymer gel was substantially mitigated, measuring only 16.6%. Finally, the gelation mechanism of the polymer gel was scrutinized in conjunction with microscopic morphology analysis. We expect that this study will not only contribute to the effective development of deep and ultradeep oil and gas reservoirs but also furnish a theoretical foundation for practical field applications.

The utilization of CO₂ foam gel fracturing fluid offers several significant advantages, including minimal reservoir damage, reduced water consumption during application, enhanced cleaning efficiency, and additional beneficial properties. However, several current CO₂ foam gel fracturing fluid systems face challenges, such as complex preparation processes and insufficient viscosity, which limit their proppant transport capacity. To address these issues, this work develops a novel CO₂ foam gel fracturing fluid system characterized by simple preparation and robust foam stability. This system was optimized by incorporating a thickening agent CZJ-1 in conjunction with a foaming agent YFP-1. The results of static sand-carrying experiments indicate that under varying temperatures and sand–fluid ratio conditions, the proppant settling velocity is significantly low. Furthermore, the static sand-carrying capacity of the CO₂ foam gel fracturing fluid exceeds that of the base fluid. The stable and dense foam gel effectively encapsulates the proppant, thereby improving sand-carrying capacity. In high-temperature shear tests, conducted at a shear rate of 170 s⁻¹ and a temperature of 110 °C for 90 min, the apparent viscosity of the CO₂ foam gel fracturing fluid remained above 20 mPa·s after shear, demonstrating excellent high-temperature shear resistance. This work introduces a novel CO₂ foam gel fracturing fluid system that is specifically tailored for low-permeability reservoir fracturing and extraction. The system shows significant promise for the efficient development of low-pressure, low-permeability, and water-sensitive reservoirs, as well as for the effective utilization and sequestration of CO₂.

To address the problem of serious gas channeling during CO₂ flooding in low-permeability reservoirs, which leads to poor oil recovery, this study developed a CO₂-resistant gel using a novel CO₂-responsive polymer (ADA) for gas channel control. The ADA polymer was synthesized via free-radical copolymerization of acrylamide (AM), dimethylaminopropyl methacrylamide (DMAPMA), and 2-acrylamido-2-methylpropanesulfonic acid (AMPS), which introduced protonatable tertiary-amine groups and sulfonate moieties into the polymer backbone. Comprehensive characterizations confirmed the designed structure and adequate thermal stability of the ADA polymer. Rheological tests demonstrated that the ADA polymer solution exhibits significant CO₂-triggered viscosity enhancement and excellent shear resistance. When crosslinked with phenolic resin, the resulting ADA gel showed outstanding CO₂ tolerance under simulated reservoir conditions (110 °C, 10 MPa). After 600 s of CO₂ exposure, the ADA gel retained over 99% of its initial viscosity, whereas a conventional HPAM-based industrial gel degraded to 61% of its original viscosity. The CO₂-resistance mechanism involves protonation of tertiary amines to form quaternary ammonium salts, which electrostatically interact with sulfonate groups, creating a reinforced dual-crosslinked network that effectively protects the gel from H⁺ ion attack. Core flooding experiments confirmed its ability to enhance oil recovery by plugging high-permeability channels and diverting flow, achieving a final recovery of up to 48.5% in heterogeneous cores. This work provides a novel gel system for improving sweep efficiency and storage security during CO₂ flooding in low-permeability reservoirs.

CO₂ flooding is an effective technique for enhancing oil recovery in low-permeability reservoirs. However, it is often hindered by severe CO₂ channeling. This challenge is particularly pronounced in near-wellbore regions with large pressure differentials and in fractured reservoirs, where high CO₂ injection rates and rapid breakthrough require channel blocking systems with high mechanical strength and excellent CO₂-resistant performance. In this work, a smart responsive polymer was synthesized and subsequently crosslinked with a highly active phenolic resin crosslinking agent to develop a smart responsive polymer gel channel blocking system. The resulting gel exhibits CO₂-responsive strength enhancement and excellent CO₂-resistant performance. The static and dynamic gelation behaviors, nonlinear rheological properties, CO₂-resistant performance, channel blocking, and enhanced oil recovery performance of the smart responsive polymer gel were systematically investigated. The results demonstrate that the polymer gel maintains good structural stability during dynamic transport in the reservoir and does not undergo significant strength degradation under shear conditions. Moreover, the smart responsive polymer gel exhibits excellent CO₂-resistant performance within a temperature range of 80–110 °C, salinity up to 10 × 10⁴ mg/L, and pressure up to 20 MPa. Moreover, the system shows a significant enhancement in channel blocking and enhanced oil recovery performance, highlighting its promising potential for effective CO₂ flooding channel blocking in low-permeability reservoirs.