Single- and bi-layer MoS ₂ are two-dimensional semiconductors able to withstand very large deformations before failure, standing out as suitable templates for strain engineering applications and flexible electronics. It is imperative, for the proper integration of this material in practical applications, that the relationship between material property and strain is well understood. Two dimensional MoS ₂ crystals fabricated by chemical vapor deposition or micromechanical exfoliation are transferred onto flexible substrates and subjected to biaxial tension on a carefully designed and assessed loading stage with high accuracy and control. The successful stress transfer from substrate to the overlying 2D crystal is identified by in-situ monitoring of the strain-induced phonon frequency and photoluminescence peak shifts. Reliable values for the mode Grüneisen parameters and exciton deformation potentials were obtained by studying a significant number of crystals. The experimental results are backed by density functional theory calculations and are in good agreement with the experiments. This work highlights the potential of these materials in strain engineering applications and gives accurate values for single- and bi-layer MoS ₂ thermomechanical parameters.

Ultrathin NiO films in the thickness range between 1 and 27 nm have been deposited on high-quality quartz substrates by direct magnetron sputtering under a rough vacuum with a base pressure of 2 × 10⁻² mbar. The sputtering target was metallic Ni; however, due to the rough vacuum a precursor material was grown in which most of Ni was already oxidized. Subsequent short annealing at temperatures of about 600 °C in a furnace in air resulted in NiO with high crystallinity quality, as atomic force microscopy revealed. The images of surface morphology showed that the NiO films were continuous and follow a normal grain growth mode. UV-Vis light absorption spectroscopy experiments have revealed a blue shift of the direct band gap of NiO. The band gap was determined either by Tauc plots (onset) or by the derivative method (highest rate of absorbance increase just after the onset). The experimental results are interpreted as evidences of quantum confinement effects. Theoretical calculations based on Hartree Fock approximation as applied for an electron-hole system, in the framework of effective mass approximation were carried out. The agreement between theory and experiment supports the quantum confinement interpretation.

In this study, the localized surface plasmon resonances (LSPRs) of Ag nanoparticles (NPs) embedded in ZnO dielectric matrices were studied. Initially, continuous Ag thin films were deposited on Corning glass substrates via magnetron sputtering, followed by post annealing, resulting in the formation of self-assembled nanoparticles. In some cases, a heated substrate holder was employed to induce NP formation during the deposition. The morphology of nanoparticles was studied using atomic force microscopy (AFM). Ultraviolet–visible spectroscopy (UV-Vis) probed the LSPRs. Subsequently, a 70 nm thick ZnO layer was deposited on top of the Ag thin films. For the Ag films, LSPR characteristics were found to depend on the initial film thickness. The ZnO capping layer induced an intense red shift, suggesting its potential as a mechanism for tailoring LSPRs. Lastly, theoretical calculations with the rigorous coupled-wave analysis (RCWA) method were carried out for comparison with the experimental results.