In this study, the effect of Zn and Ca addition on microstructure and strength at room temperature of Mg-Sn alloys was investigated by comparison of Mg-6Sn, Mg-6Sn-2Zn, and Mg-6Sn-2Zn-1Ca alloys in as-cast and as-extruded states. In the as-cast samples, α-Mg and Mg₂Sn phases were the main phases of Mg-6Sn and Mg-6Sn-2Zn alloys, while the CaMgSn phase was formed in Mg-6Sn-2Zn-1Ca alloy due to the addition of the Ca element. Mg₂Sn phase dissolved into the matrix during homogenization while CaMgSn phase remained. Incomplete dynamic recrystallization (DRX) took place in these alloys during hot extrusion. Fine Mg₂Sn precipitates were observed in α-Mg matrix of as-extruded samples. Zn showed little influence on microstructure, whereas Ca reduced the volume fraction of un-DRXed grains and increased the size of DRXed grains. As-extruded Mg-Sn alloys exhibited typical fiber texture. The strength at room temperature of Mg-Sn alloys improved significantly after hot extrusion. The addition of Zn element was beneficial to the strength at room temperature of the Mg-6Sn alloy, while the further addition of Ca element was harmful to the strength. Among these alloys, the Mg-6Sn-2Zn alloy exhibited the best strength at room temperature in both as-cast and as-extruded states.

The effects of the extrusion process and CaO addition amount on microstructure, mechanical, and corrosion properties of AZ31 alloys were investigated by means of optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), standard tensile testing, and so on. The grain size of AZ31 or AZ31-1%CaO alloy becomes larger with increasing extrusion temperature. The grain size of AZ31-1%CaO alloy is much smaller than that of AZ31 alloy at the same extrusion temperature. In addition, the formation of the Al₂Ca phase caused by CaO addition refines the grain size, and the recrystallization of AZ31-1%CaO alloy is improved significantly. The recrystallization grains distribute more uniformly as the increase of extrusion ratio, and the completely recrystallized grains distribute uniformly in the form of equiaxed crystals with an extrusion ratio of 9. Tensile testing results show that extruded AZ31-1%CaO alloy at the extrusion temperature of 300 °C and an extrusion ratio of 9 exhibits the best mechanical properties. While corrosion properties of AZ31 alloys decreases due to the addition of CaO.

In this study, as-cast Mg–6Sn–2Zn (wt.%) alloy was subjected to friction stir processing (FSP) and the microstructure and tensile properties of FSP Mg–6Sn–2Zn samples were investigated. It was found that, in the stir zone (SZ) of FSP Mg–6Sn–2Zn samples, α-Mg grains were significantly refined via dynamic recrystallization (DRX) and the Mg₂Sn phase was broken and partially dissolved. The microstructure in SZ was nonuniform and DRXed grains in the SZ-up regions were coarser than those in the SZ-down regions. Coarse broken Mg₂Sn particles were observed in the SZ-up regions, while only fine Mg₂Sn particles were observed in the SZ-down regions. Strong {0001} basal texture developed in the SZ regions of Mg–6Sn–2Zn samples after FSP. The increase of travel speed had little effect on the texture of different SZ regions. The ductility of FSP Mg–6Sn–2Zn samples was obviously improved, while the improvement in strength was negligible when compared to the as-cast sample. The tensile properties of FSP Mg–6Sn–2Zn samples were influenced by grain refinement, texture modification, and the breaking up and dissolution of the Mg₂Sn phase.